C17510 Copper vs. ASTM Grade LC9 Steel
C17510 copper belongs to the copper alloys classification, while ASTM grade LC9 steel belongs to the iron alloys. There are 26 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is C17510 copper and the bottom bar is ASTM grade LC9 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 190 |
| Elongation at Break, % | 5.4 to 37 | |
| 22 |
| Poisson's Ratio | 0.34 | |
| 0.29 |
| Shear Modulus, GPa | 44 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 310 to 860 | |
| 660 |
| Tensile Strength: Yield (Proof), MPa | 120 to 750 | |
| 590 |
Thermal Properties
| Latent Heat of Fusion, J/g | 220 | |
| 260 |
| Maximum Temperature: Mechanical, °C | 220 | |
| 430 |
| Melting Completion (Liquidus), °C | 1070 | |
| 1450 |
| Melting Onset (Solidus), °C | 1030 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 470 |
| Thermal Expansion, µm/m-K | 17 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 22 to 54 | |
| 8.9 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 23 to 54 | |
| 10 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 49 | |
| 8.0 |
| Density, g/cm3 | 8.9 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 4.2 | |
| 2.3 |
| Embodied Energy, MJ/kg | 65 | |
| 31 |
| Embodied Water, L/kg | 310 | |
| 65 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 39 to 92 | |
| 140 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 64 to 2410 | |
| 920 |
| Stiffness to Weight: Axial, points | 7.4 | |
| 13 |
| Stiffness to Weight: Bending, points | 18 | |
| 24 |
| Strength to Weight: Axial, points | 9.7 to 27 | |
| 23 |
| Strength to Weight: Bending, points | 11 to 23 | |
| 21 |
| Thermal Shock Resistance, points | 11 to 30 | |
| 20 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 to 0.2 | |
| 0 |
| Beryllium (Be), % | 0.2 to 0.6 | |
| 0 |
| Carbon (C), % | 0 | |
| 0 to 0.13 |
| Chromium (Cr), % | 0 | |
| 0 to 0.5 |
| Cobalt (Co), % | 0 to 0.3 | |
| 0 |
| Copper (Cu), % | 95.9 to 98.4 | |
| 0 to 0.3 |
| Iron (Fe), % | 0 to 0.1 | |
| 87.4 to 91.5 |
| Manganese (Mn), % | 0 | |
| 0 to 0.9 |
| Molybdenum (Mo), % | 0 | |
| 0 to 0.2 |
| Nickel (Ni), % | 1.4 to 2.2 | |
| 8.5 to 10 |
| Phosphorus (P), % | 0 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 0.2 | |
| 0 to 0.45 |
| Sulfur (S), % | 0 | |
| 0 to 0.045 |
| Vanadium (V), % | 0 | |
| 0 to 0.030 |
| Residuals, % | 0 to 0.5 | |
| 0 |