C18100 Copper vs. C69710 Brass
Both C18100 copper and C69710 brass are copper alloys. Both are furnished in the H04 (full hard) temper. They have 78% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is C18100 copper and the bottom bar is C69710 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 110 |
| Elongation at Break, % | 8.3 | |
| 25 |
| Poisson's Ratio | 0.34 | |
| 0.32 |
| Shear Modulus, GPa | 47 | |
| 41 |
| Shear Strength, MPa | 300 | |
| 300 |
| Tensile Strength: Ultimate (UTS), MPa | 510 | |
| 470 |
| Tensile Strength: Yield (Proof), MPa | 460 | |
| 230 |
Thermal Properties
| Latent Heat of Fusion, J/g | 210 | |
| 240 |
| Maximum Temperature: Mechanical, °C | 200 | |
| 160 |
| Melting Completion (Liquidus), °C | 1080 | |
| 930 |
| Melting Onset (Solidus), °C | 1020 | |
| 880 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 400 |
| Thermal Conductivity, W/m-K | 320 | |
| 40 |
| Thermal Expansion, µm/m-K | 17 | |
| 19 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 80 | |
| 8.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 81 | |
| 8.7 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 31 | |
| 26 |
| Density, g/cm3 | 8.9 | |
| 8.3 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 2.7 |
| Embodied Energy, MJ/kg | 43 | |
| 44 |
| Embodied Water, L/kg | 310 | |
| 310 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 40 | |
| 99 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 900 | |
| 250 |
| Stiffness to Weight: Axial, points | 7.3 | |
| 7.3 |
| Stiffness to Weight: Bending, points | 18 | |
| 19 |
| Strength to Weight: Axial, points | 16 | |
| 16 |
| Strength to Weight: Bending, points | 16 | |
| 16 |
| Thermal Diffusivity, mm2/s | 94 | |
| 12 |
| Thermal Shock Resistance, points | 18 | |
| 16 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Arsenic (As), % | 0 | |
| 0.030 to 0.060 |
| Chromium (Cr), % | 0.4 to 1.2 | |
| 0 |
| Copper (Cu), % | 98.7 to 99.49 | |
| 75 to 80 |
| Iron (Fe), % | 0 | |
| 0 to 0.2 |
| Lead (Pb), % | 0 | |
| 0.5 to 1.5 |
| Magnesium (Mg), % | 0.030 to 0.060 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 0 to 0.4 |
| Silicon (Si), % | 0 | |
| 2.5 to 3.5 |
| Zinc (Zn), % | 0 | |
| 13.8 to 22 |
| Zirconium (Zr), % | 0.080 to 0.2 | |
| 0 |
| Residuals, % | 0 to 0.5 | |
| 0 to 0.5 |