C19000 Copper vs. C37000 Muntz Metal
Both C19000 copper and C37000 Muntz Metal are copper alloys. They have 61% of their average alloy composition in common.
For each property being compared, the top bar is C19000 copper and the bottom bar is C37000 Muntz Metal.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 100 |
| Elongation at Break, % | 2.5 to 50 | |
| 40 |
| Poisson's Ratio | 0.34 | |
| 0.31 |
| Rockwell B Hardness | 45 to 94 | |
| 45 |
| Shear Modulus, GPa | 43 | |
| 39 |
| Shear Strength, MPa | 170 to 390 | |
| 270 |
| Tensile Strength: Ultimate (UTS), MPa | 260 to 760 | |
| 400 |
| Tensile Strength: Yield (Proof), MPa | 140 to 630 | |
| 160 |
Thermal Properties
| Latent Heat of Fusion, J/g | 210 | |
| 170 |
| Maximum Temperature: Mechanical, °C | 200 | |
| 120 |
| Melting Completion (Liquidus), °C | 1080 | |
| 900 |
| Melting Onset (Solidus), °C | 1040 | |
| 890 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 380 |
| Thermal Conductivity, W/m-K | 250 | |
| 120 |
| Thermal Expansion, µm/m-K | 17 | |
| 21 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 60 | |
| 27 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 61 | |
| 30 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 31 | |
| 23 |
| Density, g/cm3 | 8.9 | |
| 8.1 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 2.7 |
| Embodied Energy, MJ/kg | 42 | |
| 45 |
| Embodied Water, L/kg | 310 | |
| 320 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 18 to 110 | |
| 130 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 89 to 1730 | |
| 120 |
| Stiffness to Weight: Axial, points | 7.2 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 18 | |
| 19 |
| Strength to Weight: Axial, points | 8.2 to 24 | |
| 14 |
| Strength to Weight: Bending, points | 10 to 21 | |
| 15 |
| Thermal Diffusivity, mm2/s | 73 | |
| 39 |
| Thermal Shock Resistance, points | 9.3 to 27 | |
| 13 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Copper (Cu), % | 96.9 to 99 | |
| 59 to 62 |
| Iron (Fe), % | 0 to 0.1 | |
| 0 to 0.15 |
| Lead (Pb), % | 0 to 0.050 | |
| 0.8 to 1.5 |
| Nickel (Ni), % | 0.9 to 1.3 | |
| 0 |
| Phosphorus (P), % | 0.15 to 0.35 | |
| 0 |
| Zinc (Zn), % | 0 to 0.8 | |
| 36 to 40.2 |
| Residuals, % | 0 to 0.5 | |
| 0 to 0.4 |