C19010 Copper vs. C93800 Bronze
Both C19010 copper and C93800 bronze are copper alloys. They have 78% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is C19010 copper and the bottom bar is C93800 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 96 |
| Elongation at Break, % | 2.4 to 22 | |
| 9.7 |
| Poisson's Ratio | 0.34 | |
| 0.35 |
| Shear Modulus, GPa | 43 | |
| 35 |
| Tensile Strength: Ultimate (UTS), MPa | 330 to 640 | |
| 200 |
| Tensile Strength: Yield (Proof), MPa | 260 to 620 | |
| 120 |
Thermal Properties
| Latent Heat of Fusion, J/g | 210 | |
| 170 |
| Maximum Temperature: Mechanical, °C | 200 | |
| 140 |
| Melting Completion (Liquidus), °C | 1060 | |
| 940 |
| Melting Onset (Solidus), °C | 1010 | |
| 850 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 340 |
| Thermal Conductivity, W/m-K | 260 | |
| 52 |
| Thermal Expansion, µm/m-K | 17 | |
| 19 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 48 to 63 | |
| 11 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 48 to 63 | |
| 11 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 31 | |
| 31 |
| Density, g/cm3 | 8.9 | |
| 9.1 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 3.2 |
| Embodied Energy, MJ/kg | 42 | |
| 51 |
| Embodied Water, L/kg | 310 | |
| 380 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 7.3 to 140 | |
| 17 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 290 to 1680 | |
| 70 |
| Stiffness to Weight: Axial, points | 7.3 | |
| 5.9 |
| Stiffness to Weight: Bending, points | 18 | |
| 17 |
| Strength to Weight: Axial, points | 10 to 20 | |
| 6.1 |
| Strength to Weight: Bending, points | 12 to 18 | |
| 8.4 |
| Thermal Diffusivity, mm2/s | 75 | |
| 17 |
| Thermal Shock Resistance, points | 12 to 23 | |
| 8.1 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 | |
| 0 to 0.0050 |
| Antimony (Sb), % | 0 | |
| 0 to 0.8 |
| Copper (Cu), % | 97.3 to 99.04 | |
| 75 to 79 |
| Iron (Fe), % | 0 | |
| 0 to 0.15 |
| Lead (Pb), % | 0 | |
| 13 to 16 |
| Nickel (Ni), % | 0.8 to 1.8 | |
| 0 to 1.0 |
| Phosphorus (P), % | 0.010 to 0.050 | |
| 0 to 1.5 |
| Silicon (Si), % | 0.15 to 0.35 | |
| 0 to 0.0050 |
| Sulfur (S), % | 0 | |
| 0 to 0.080 |
| Tin (Sn), % | 0 | |
| 6.3 to 7.5 |
| Zinc (Zn), % | 0 | |
| 0 to 0.8 |
| Residuals, % | 0 to 0.5 | |
| 0 to 1.0 |