C19020 Copper vs. C17510 Copper
Both C19020 copper and C17510 copper are copper alloys. Their average alloy composition is basically identical. There are 26 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is C19020 copper and the bottom bar is C17510 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 120 |
| Elongation at Break, % | 2.3 to 5.7 | |
| 5.4 to 37 |
| Poisson's Ratio | 0.34 | |
| 0.34 |
| Shear Modulus, GPa | 44 | |
| 44 |
| Shear Strength, MPa | 260 to 340 | |
| 210 to 500 |
| Tensile Strength: Ultimate (UTS), MPa | 440 to 590 | |
| 310 to 860 |
Thermal Properties
| Latent Heat of Fusion, J/g | 210 | |
| 220 |
| Maximum Temperature: Mechanical, °C | 200 | |
| 220 |
| Melting Completion (Liquidus), °C | 1090 | |
| 1070 |
| Melting Onset (Solidus), °C | 1030 | |
| 1030 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 390 |
| Thermal Conductivity, W/m-K | 190 | |
| 210 |
| Thermal Expansion, µm/m-K | 17 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 50 | |
| 22 to 54 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 50 | |
| 23 to 54 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 31 | |
| 49 |
| Density, g/cm3 | 8.9 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 2.8 | |
| 4.2 |
| Embodied Energy, MJ/kg | 44 | |
| 65 |
| Embodied Water, L/kg | 310 | |
| 310 |
Common Calculations
| Stiffness to Weight: Axial, points | 7.2 | |
| 7.4 |
| Stiffness to Weight: Bending, points | 18 | |
| 18 |
| Strength to Weight: Axial, points | 14 to 18 | |
| 9.7 to 27 |
| Strength to Weight: Bending, points | 14 to 18 | |
| 11 to 23 |
| Thermal Diffusivity, mm2/s | 55 | |
| 60 |
| Thermal Shock Resistance, points | 16 to 21 | |
| 11 to 30 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 | |
| 0 to 0.2 |
| Beryllium (Be), % | 0 | |
| 0.2 to 0.6 |
| Cobalt (Co), % | 0 | |
| 0 to 0.3 |
| Copper (Cu), % | 95.7 to 99.19 | |
| 95.9 to 98.4 |
| Iron (Fe), % | 0 | |
| 0 to 0.1 |
| Nickel (Ni), % | 0.5 to 3.0 | |
| 1.4 to 2.2 |
| Phosphorus (P), % | 0.010 to 0.2 | |
| 0 |
| Silicon (Si), % | 0 | |
| 0 to 0.2 |
| Tin (Sn), % | 0.3 to 0.9 | |
| 0 |
| Residuals, % | 0 to 0.2 | |
| 0 to 0.5 |