C19020 Copper vs. C19010 Copper
Both C19020 copper and C19010 copper are copper alloys. They have a very high 99% of their average alloy composition in common. There are 26 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is C19020 copper and the bottom bar is C19010 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 120 |
| Elongation at Break, % | 2.3 to 5.7 | |
| 2.4 to 22 |
| Poisson's Ratio | 0.34 | |
| 0.34 |
| Shear Modulus, GPa | 44 | |
| 43 |
| Shear Strength, MPa | 260 to 340 | |
| 210 to 360 |
| Tensile Strength: Ultimate (UTS), MPa | 440 to 590 | |
| 330 to 640 |
Thermal Properties
| Latent Heat of Fusion, J/g | 210 | |
| 210 |
| Maximum Temperature: Mechanical, °C | 200 | |
| 200 |
| Melting Completion (Liquidus), °C | 1090 | |
| 1060 |
| Melting Onset (Solidus), °C | 1030 | |
| 1010 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 390 |
| Thermal Conductivity, W/m-K | 190 | |
| 260 |
| Thermal Expansion, µm/m-K | 17 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 50 | |
| 48 to 63 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 50 | |
| 48 to 63 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 31 | |
| 31 |
| Density, g/cm3 | 8.9 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 2.8 | |
| 2.7 |
| Embodied Energy, MJ/kg | 44 | |
| 42 |
| Embodied Water, L/kg | 310 | |
| 310 |
Common Calculations
| Stiffness to Weight: Axial, points | 7.2 | |
| 7.3 |
| Stiffness to Weight: Bending, points | 18 | |
| 18 |
| Strength to Weight: Axial, points | 14 to 18 | |
| 10 to 20 |
| Strength to Weight: Bending, points | 14 to 18 | |
| 12 to 18 |
| Thermal Diffusivity, mm2/s | 55 | |
| 75 |
| Thermal Shock Resistance, points | 16 to 21 | |
| 12 to 23 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Copper (Cu), % | 95.7 to 99.19 | |
| 97.3 to 99.04 |
| Nickel (Ni), % | 0.5 to 3.0 | |
| 0.8 to 1.8 |
| Phosphorus (P), % | 0.010 to 0.2 | |
| 0.010 to 0.050 |
| Silicon (Si), % | 0 | |
| 0.15 to 0.35 |
| Tin (Sn), % | 0.3 to 0.9 | |
| 0 |
| Residuals, % | 0 to 0.2 | |
| 0 to 0.5 |