C19020 Copper vs. C38500 Bronze
Both C19020 copper and C38500 bronze are copper alloys. They have 57% of their average alloy composition in common. There are 26 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is C19020 copper and the bottom bar is C38500 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 100 |
| Elongation at Break, % | 2.3 to 5.7 | |
| 17 |
| Poisson's Ratio | 0.34 | |
| 0.31 |
| Shear Modulus, GPa | 44 | |
| 37 |
| Shear Strength, MPa | 260 to 340 | |
| 230 |
| Tensile Strength: Ultimate (UTS), MPa | 440 to 590 | |
| 370 |
Thermal Properties
| Latent Heat of Fusion, J/g | 210 | |
| 160 |
| Maximum Temperature: Mechanical, °C | 200 | |
| 110 |
| Melting Completion (Liquidus), °C | 1090 | |
| 890 |
| Melting Onset (Solidus), °C | 1030 | |
| 880 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 380 |
| Thermal Conductivity, W/m-K | 190 | |
| 120 |
| Thermal Expansion, µm/m-K | 17 | |
| 21 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 50 | |
| 28 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 50 | |
| 31 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 31 | |
| 22 |
| Density, g/cm3 | 8.9 | |
| 8.1 |
| Embodied Carbon, kg CO2/kg material | 2.8 | |
| 2.6 |
| Embodied Energy, MJ/kg | 44 | |
| 45 |
| Embodied Water, L/kg | 310 | |
| 320 |
Common Calculations
| Stiffness to Weight: Axial, points | 7.2 | |
| 7.0 |
| Stiffness to Weight: Bending, points | 18 | |
| 19 |
| Strength to Weight: Axial, points | 14 to 18 | |
| 13 |
| Strength to Weight: Bending, points | 14 to 18 | |
| 14 |
| Thermal Diffusivity, mm2/s | 55 | |
| 40 |
| Thermal Shock Resistance, points | 16 to 21 | |
| 12 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Copper (Cu), % | 95.7 to 99.19 | |
| 55 to 59 |
| Iron (Fe), % | 0 | |
| 0 to 0.35 |
| Lead (Pb), % | 0 | |
| 2.5 to 3.5 |
| Nickel (Ni), % | 0.5 to 3.0 | |
| 0 |
| Phosphorus (P), % | 0.010 to 0.2 | |
| 0 |
| Tin (Sn), % | 0.3 to 0.9 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 36.7 to 42.5 |
| Residuals, % | 0 to 0.2 | |
| 0 to 0.5 |