C19020 Copper vs. C62300 Bronze
Both C19020 copper and C62300 bronze are copper alloys. They have 87% of their average alloy composition in common. There are 26 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is C19020 copper and the bottom bar is C62300 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 110 |
| Elongation at Break, % | 2.3 to 5.7 | |
| 18 to 32 |
| Poisson's Ratio | 0.34 | |
| 0.34 |
| Shear Modulus, GPa | 44 | |
| 43 |
| Shear Strength, MPa | 260 to 340 | |
| 360 to 390 |
| Tensile Strength: Ultimate (UTS), MPa | 440 to 590 | |
| 570 to 630 |
Thermal Properties
| Latent Heat of Fusion, J/g | 210 | |
| 230 |
| Maximum Temperature: Mechanical, °C | 200 | |
| 220 |
| Melting Completion (Liquidus), °C | 1090 | |
| 1050 |
| Melting Onset (Solidus), °C | 1030 | |
| 1040 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 440 |
| Thermal Conductivity, W/m-K | 190 | |
| 54 |
| Thermal Expansion, µm/m-K | 17 | |
| 18 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 50 | |
| 12 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 50 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 31 | |
| 28 |
| Density, g/cm3 | 8.9 | |
| 8.3 |
| Embodied Carbon, kg CO2/kg material | 2.8 | |
| 3.1 |
| Embodied Energy, MJ/kg | 44 | |
| 52 |
| Embodied Water, L/kg | 310 | |
| 390 |
Common Calculations
| Stiffness to Weight: Axial, points | 7.2 | |
| 7.6 |
| Stiffness to Weight: Bending, points | 18 | |
| 19 |
| Strength to Weight: Axial, points | 14 to 18 | |
| 19 to 21 |
| Strength to Weight: Bending, points | 14 to 18 | |
| 18 to 20 |
| Thermal Diffusivity, mm2/s | 55 | |
| 15 |
| Thermal Shock Resistance, points | 16 to 21 | |
| 20 to 22 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 | |
| 8.5 to 10 |
| Copper (Cu), % | 95.7 to 99.19 | |
| 83.2 to 89.5 |
| Iron (Fe), % | 0 | |
| 2.0 to 4.0 |
| Manganese (Mn), % | 0 | |
| 0 to 0.5 |
| Nickel (Ni), % | 0.5 to 3.0 | |
| 0 to 1.0 |
| Phosphorus (P), % | 0.010 to 0.2 | |
| 0 |
| Silicon (Si), % | 0 | |
| 0 to 0.25 |
| Tin (Sn), % | 0.3 to 0.9 | |
| 0 to 0.6 |
| Residuals, % | 0 to 0.2 | |
| 0 to 0.5 |