C19020 Copper vs. ZA-8
C19020 copper belongs to the copper alloys classification, while ZA-8 belongs to the zinc alloys. There are 26 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is C19020 copper and the bottom bar is ZA-8.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 85 to 86 |
| Elongation at Break, % | 2.3 to 5.7 | |
| 1.3 to 8.0 |
| Poisson's Ratio | 0.34 | |
| 0.26 |
| Shear Modulus, GPa | 44 | |
| 34 |
| Shear Strength, MPa | 260 to 340 | |
| 240 to 280 |
| Tensile Strength: Ultimate (UTS), MPa | 440 to 590 | |
| 210 to 370 |
Thermal Properties
| Latent Heat of Fusion, J/g | 210 | |
| 110 |
| Maximum Temperature: Mechanical, °C | 200 | |
| 100 |
| Melting Completion (Liquidus), °C | 1090 | |
| 400 |
| Melting Onset (Solidus), °C | 1030 | |
| 380 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 440 |
| Thermal Conductivity, W/m-K | 190 | |
| 120 |
| Thermal Expansion, µm/m-K | 17 | |
| 23 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 50 | |
| 28 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 50 | |
| 40 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 31 | |
| 11 |
| Density, g/cm3 | 8.9 | |
| 6.3 |
| Embodied Carbon, kg CO2/kg material | 2.8 | |
| 3.3 |
| Embodied Energy, MJ/kg | 44 | |
| 62 |
| Embodied Water, L/kg | 310 | |
| 420 |
Common Calculations
| Stiffness to Weight: Axial, points | 7.2 | |
| 7.5 |
| Stiffness to Weight: Bending, points | 18 | |
| 23 |
| Strength to Weight: Axial, points | 14 to 18 | |
| 9.3 to 17 |
| Strength to Weight: Bending, points | 14 to 18 | |
| 12 to 18 |
| Thermal Diffusivity, mm2/s | 55 | |
| 42 |
| Thermal Shock Resistance, points | 16 to 21 | |
| 7.6 to 13 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 | |
| 8.0 to 8.8 |
| Cadmium (Cd), % | 0 | |
| 0 to 0.0060 |
| Copper (Cu), % | 95.7 to 99.19 | |
| 0.8 to 1.3 |
| Iron (Fe), % | 0 | |
| 0 to 0.075 |
| Lead (Pb), % | 0 | |
| 0 to 0.0060 |
| Magnesium (Mg), % | 0 | |
| 0.015 to 0.030 |
| Nickel (Ni), % | 0.5 to 3.0 | |
| 0 to 0.020 |
| Phosphorus (P), % | 0.010 to 0.2 | |
| 0 |
| Silicon (Si), % | 0 | |
| 0 to 0.045 |
| Tin (Sn), % | 0.3 to 0.9 | |
| 0 to 0.0030 |
| Zinc (Zn), % | 0 | |
| 89.7 to 91.2 |
| Residuals, % | 0 to 0.2 | |
| 0 |