C19400 Copper vs. R60706 Alloy
C19400 copper belongs to the copper alloys classification, while R60706 alloy belongs to the otherwise unclassified metals. There are 20 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is C19400 copper and the bottom bar is R60706 alloy.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 98 |
| Elongation at Break, % | 2.3 to 37 | |
| 16 |
| Poisson's Ratio | 0.34 | |
| 0.34 |
| Shear Modulus, GPa | 44 | |
| 37 |
| Tensile Strength: Ultimate (UTS), MPa | 310 to 630 | |
| 580 |
| Tensile Strength: Yield (Proof), MPa | 98 to 520 | |
| 390 |
Thermal Properties
| Latent Heat of Fusion, J/g | 210 | |
| 250 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 270 |
| Thermal Conductivity, W/m-K | 260 | |
| 17 |
| Thermal Expansion, µm/m-K | 17 | |
| 6.3 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.9 | |
| 6.7 |
| Embodied Water, L/kg | 300 | |
| 450 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 5.5 to 220 | |
| 82 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 41 to 1140 | |
| 760 |
| Stiffness to Weight: Axial, points | 7.3 | |
| 8.1 |
| Stiffness to Weight: Bending, points | 18 | |
| 23 |
| Strength to Weight: Axial, points | 9.7 to 20 | |
| 24 |
| Strength to Weight: Bending, points | 11 to 18 | |
| 23 |
| Thermal Diffusivity, mm2/s | 75 | |
| 9.5 |
| Thermal Shock Resistance, points | 11 to 22 | |
| 67 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Carbon (C), % | 0 | |
| 0 to 0.050 |
| Chromium (Cr), % | 0 | |
| 0 to 0.2 |
| Copper (Cu), % | 96.8 to 97.8 | |
| 0 |
| Hafnium (Hf), % | 0 | |
| 0 to 4.5 |
| Hydrogen (H), % | 0 | |
| 0 to 0.0050 |
| Iron (Fe), % | 2.1 to 2.6 | |
| 0 to 0.2 |
| Lead (Pb), % | 0 to 0.030 | |
| 0 |
| Niobium (Nb), % | 0 | |
| 2.0 to 3.0 |
| Nitrogen (N), % | 0 | |
| 0 to 0.025 |
| Oxygen (O), % | 0 | |
| 0 to 0.16 |
| Phosphorus (P), % | 0.015 to 0.15 | |
| 0 |
| Zinc (Zn), % | 0.050 to 0.2 | |
| 0 |
| Zirconium (Zr), % | 0 | |
| 91 to 98 |
| Residuals, % | 0 to 0.2 | |
| 0 |