C19800 Copper vs. N07776 Nickel
C19800 copper belongs to the copper alloys classification, while N07776 nickel belongs to the nickel alloys. There are 25 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is C19800 copper and the bottom bar is N07776 nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 200 |
| Elongation at Break, % | 9.0 to 12 | |
| 39 |
| Poisson's Ratio | 0.34 | |
| 0.3 |
| Shear Modulus, GPa | 43 | |
| 79 |
| Shear Strength, MPa | 260 to 330 | |
| 470 |
| Tensile Strength: Ultimate (UTS), MPa | 430 to 550 | |
| 700 |
| Tensile Strength: Yield (Proof), MPa | 420 to 550 | |
| 270 |
Thermal Properties
| Latent Heat of Fusion, J/g | 210 | |
| 320 |
| Maximum Temperature: Mechanical, °C | 200 | |
| 970 |
| Melting Completion (Liquidus), °C | 1070 | |
| 1550 |
| Melting Onset (Solidus), °C | 1050 | |
| 1500 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 430 |
| Thermal Expansion, µm/m-K | 18 | |
| 12 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 30 | |
| 85 |
| Density, g/cm3 | 8.9 | |
| 8.6 |
| Embodied Carbon, kg CO2/kg material | 2.8 | |
| 15 |
| Embodied Energy, MJ/kg | 43 | |
| 210 |
| Embodied Water, L/kg | 320 | |
| 270 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 49 to 52 | |
| 220 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 770 to 1320 | |
| 180 |
| Stiffness to Weight: Axial, points | 7.2 | |
| 13 |
| Stiffness to Weight: Bending, points | 18 | |
| 23 |
| Strength to Weight: Axial, points | 14 to 17 | |
| 22 |
| Strength to Weight: Bending, points | 14 to 17 | |
| 20 |
| Thermal Shock Resistance, points | 15 to 20 | |
| 20 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 | |
| 0 to 2.0 |
| Carbon (C), % | 0 | |
| 0 to 0.030 |
| Chromium (Cr), % | 0 | |
| 12 to 22 |
| Copper (Cu), % | 95.7 to 99.47 | |
| 0 |
| Iron (Fe), % | 0.020 to 0.5 | |
| 0 to 24.5 |
| Magnesium (Mg), % | 0.1 to 1.0 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 0 | |
| 9.0 to 15 |
| Nickel (Ni), % | 0 | |
| 50 to 60 |
| Niobium (Nb), % | 0 | |
| 4.0 to 6.0 |
| Phosphorus (P), % | 0.010 to 0.1 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 | |
| 0 to 0.010 |
| Tin (Sn), % | 0.1 to 1.0 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 0 to 1.0 |
| Tungsten (W), % | 0 | |
| 0.5 to 2.5 |
| Zinc (Zn), % | 0.3 to 1.5 | |
| 0 |
| Residuals, % | 0 to 0.2 | |
| 0 |