C21000 Brass vs. C67500 Bronze
Both C21000 brass and C67500 bronze are copper alloys. They have 63% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is C21000 brass and the bottom bar is C67500 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 100 |
| Elongation at Break, % | 2.9 to 50 | |
| 14 to 33 |
| Poisson's Ratio | 0.34 | |
| 0.3 |
| Shear Modulus, GPa | 43 | |
| 40 |
| Shear Strength, MPa | 180 to 280 | |
| 270 to 350 |
| Tensile Strength: Ultimate (UTS), MPa | 240 to 450 | |
| 430 to 580 |
| Tensile Strength: Yield (Proof), MPa | 69 to 440 | |
| 170 to 370 |
Thermal Properties
| Latent Heat of Fusion, J/g | 200 | |
| 170 |
| Maximum Temperature: Mechanical, °C | 190 | |
| 120 |
| Melting Completion (Liquidus), °C | 1070 | |
| 890 |
| Melting Onset (Solidus), °C | 1050 | |
| 870 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 390 |
| Thermal Conductivity, W/m-K | 230 | |
| 110 |
| Thermal Expansion, µm/m-K | 18 | |
| 21 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 56 | |
| 24 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 57 | |
| 27 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 30 | |
| 23 |
| Density, g/cm3 | 8.8 | |
| 8.0 |
| Embodied Carbon, kg CO2/kg material | 2.6 | |
| 2.8 |
| Embodied Energy, MJ/kg | 42 | |
| 47 |
| Embodied Water, L/kg | 310 | |
| 330 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 13 to 100 | |
| 61 to 130 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 21 to 830 | |
| 130 to 650 |
| Stiffness to Weight: Axial, points | 7.2 | |
| 7.3 |
| Stiffness to Weight: Bending, points | 18 | |
| 20 |
| Strength to Weight: Axial, points | 7.4 to 14 | |
| 15 to 20 |
| Strength to Weight: Bending, points | 9.6 to 15 | |
| 16 to 19 |
| Thermal Diffusivity, mm2/s | 69 | |
| 34 |
| Thermal Shock Resistance, points | 8.1 to 15 | |
| 14 to 19 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 | |
| 0 to 0.25 |
| Copper (Cu), % | 94 to 96 | |
| 57 to 60 |
| Iron (Fe), % | 0 to 0.050 | |
| 0.8 to 2.0 |
| Lead (Pb), % | 0 to 0.030 | |
| 0 to 0.2 |
| Manganese (Mn), % | 0 | |
| 0.050 to 0.5 |
| Tin (Sn), % | 0 | |
| 0.5 to 1.5 |
| Zinc (Zn), % | 3.7 to 6.0 | |
| 35.1 to 41.7 |
| Residuals, % | 0 to 0.2 | |
| 0 to 0.5 |