C22000 Bronze vs. C14520 Copper
Both C22000 bronze and C14520 copper are copper alloys. They have a moderately high 90% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is C22000 bronze and the bottom bar is C14520 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 120 |
| Elongation at Break, % | 1.9 to 45 | |
| 9.0 to 9.6 |
| Poisson's Ratio | 0.33 | |
| 0.34 |
| Shear Modulus, GPa | 42 | |
| 43 |
| Shear Strength, MPa | 200 to 300 | |
| 170 to 190 |
| Tensile Strength: Ultimate (UTS), MPa | 260 to 520 | |
| 290 to 330 |
| Tensile Strength: Yield (Proof), MPa | 69 to 500 | |
| 230 to 250 |
Thermal Properties
| Latent Heat of Fusion, J/g | 200 | |
| 210 |
| Maximum Temperature: Mechanical, °C | 180 | |
| 200 |
| Melting Completion (Liquidus), °C | 1040 | |
| 1080 |
| Melting Onset (Solidus), °C | 1020 | |
| 1050 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 390 |
| Thermal Conductivity, W/m-K | 190 | |
| 320 |
| Thermal Expansion, µm/m-K | 18 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 44 | |
| 85 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 45 | |
| 85 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 29 | |
| 33 |
| Density, g/cm3 | 8.7 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 2.6 | |
| 2.6 |
| Embodied Energy, MJ/kg | 42 | |
| 42 |
| Embodied Water, L/kg | 310 | |
| 310 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 3.7 to 230 | |
| 24 to 29 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 21 to 1110 | |
| 240 to 280 |
| Stiffness to Weight: Axial, points | 7.2 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 18 | |
| 18 |
| Strength to Weight: Axial, points | 8.1 to 17 | |
| 9.0 to 10 |
| Strength to Weight: Bending, points | 10 to 17 | |
| 11 to 12 |
| Thermal Diffusivity, mm2/s | 56 | |
| 94 |
| Thermal Shock Resistance, points | 8.8 to 18 | |
| 10 to 12 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Copper (Cu), % | 89 to 91 | |
| 99.2 to 99.596 |
| Iron (Fe), % | 0 to 0.050 | |
| 0 |
| Lead (Pb), % | 0 to 0.050 | |
| 0 |
| Phosphorus (P), % | 0 | |
| 0.0040 to 0.020 |
| Tellurium (Te), % | 0 | |
| 0.4 to 0.7 |
| Zinc (Zn), % | 8.7 to 11 | |
| 0 |
| Residuals, % | 0 to 0.2 | |
| 0 |