C22600 Bronze vs. C85500 Brass
Both C22600 bronze and C85500 brass are copper alloys. They have 74% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is C22600 bronze and the bottom bar is C85500 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 100 |
| Elongation at Break, % | 2.5 to 33 | |
| 40 |
| Poisson's Ratio | 0.33 | |
| 0.31 |
| Rockwell B Hardness | 46 to 85 | |
| 55 |
| Shear Modulus, GPa | 42 | |
| 40 |
| Tensile Strength: Ultimate (UTS), MPa | 330 to 570 | |
| 410 |
| Tensile Strength: Yield (Proof), MPa | 270 to 490 | |
| 160 |
Thermal Properties
| Latent Heat of Fusion, J/g | 200 | |
| 170 |
| Maximum Temperature: Mechanical, °C | 170 | |
| 120 |
| Melting Completion (Liquidus), °C | 1040 | |
| 900 |
| Melting Onset (Solidus), °C | 1000 | |
| 890 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 390 |
| Thermal Conductivity, W/m-K | 170 | |
| 120 |
| Thermal Expansion, µm/m-K | 18 | |
| 21 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 40 | |
| 26 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 42 | |
| 29 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 28 | |
| 23 |
| Density, g/cm3 | 8.7 | |
| 8.0 |
| Embodied Carbon, kg CO2/kg material | 2.6 | |
| 2.7 |
| Embodied Energy, MJ/kg | 42 | |
| 46 |
| Embodied Water, L/kg | 310 | |
| 320 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 14 to 100 | |
| 130 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 330 to 1070 | |
| 120 |
| Stiffness to Weight: Axial, points | 7.2 | |
| 7.3 |
| Stiffness to Weight: Bending, points | 19 | |
| 20 |
| Strength to Weight: Axial, points | 11 to 18 | |
| 14 |
| Strength to Weight: Bending, points | 12 to 18 | |
| 15 |
| Thermal Diffusivity, mm2/s | 52 | |
| 38 |
| Thermal Shock Resistance, points | 11 to 19 | |
| 14 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Copper (Cu), % | 86 to 89 | |
| 59 to 63 |
| Iron (Fe), % | 0 to 0.050 | |
| 0 to 0.2 |
| Lead (Pb), % | 0 to 0.050 | |
| 0 to 0.2 |
| Manganese (Mn), % | 0 | |
| 0 to 0.2 |
| Nickel (Ni), % | 0 | |
| 0 to 0.2 |
| Tin (Sn), % | 0 | |
| 0 to 0.2 |
| Zinc (Zn), % | 10.7 to 14 | |
| 35.1 to 41 |
| Residuals, % | 0 to 0.2 | |
| 0 to 0.9 |