C23400 Brass vs. C95300 Bronze
Both C23400 brass and C95300 bronze are copper alloys. They have 83% of their average alloy composition in common. There are 22 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is C23400 brass and the bottom bar is C95300 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 110 |
| Poisson's Ratio | 0.32 | |
| 0.34 |
| Shear Modulus, GPa | 42 | |
| 42 |
| Tensile Strength: Ultimate (UTS), MPa | 370 to 640 | |
| 520 to 610 |
Thermal Properties
| Latent Heat of Fusion, J/g | 190 | |
| 230 |
| Maximum Temperature: Mechanical, °C | 160 | |
| 220 |
| Melting Completion (Liquidus), °C | 970 | |
| 1050 |
| Melting Onset (Solidus), °C | 930 | |
| 1040 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 440 |
| Thermal Conductivity, W/m-K | 120 | |
| 63 |
| Thermal Expansion, µm/m-K | 19 | |
| 18 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 27 | |
| 28 |
| Density, g/cm3 | 8.5 | |
| 8.3 |
| Embodied Carbon, kg CO2/kg material | 2.6 | |
| 3.1 |
| Embodied Energy, MJ/kg | 43 | |
| 52 |
| Embodied Water, L/kg | 320 | |
| 390 |
Common Calculations
| Stiffness to Weight: Axial, points | 7.2 | |
| 7.5 |
| Stiffness to Weight: Bending, points | 19 | |
| 19 |
| Strength to Weight: Axial, points | 12 to 21 | |
| 17 to 21 |
| Strength to Weight: Bending, points | 13 to 19 | |
| 17 to 19 |
| Thermal Diffusivity, mm2/s | 36 | |
| 17 |
| Thermal Shock Resistance, points | 12 to 22 | |
| 19 to 22 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 | |
| 9.0 to 11 |
| Copper (Cu), % | 81 to 84 | |
| 86.5 to 90.2 |
| Iron (Fe), % | 0 to 0.050 | |
| 0.8 to 1.5 |
| Lead (Pb), % | 0 to 0.050 | |
| 0 |
| Zinc (Zn), % | 15.7 to 19 | |
| 0 |
| Residuals, % | 0 to 0.2 | |
| 0 to 1.0 |