C23400 Brass vs. K93600 Alloy
C23400 brass belongs to the copper alloys classification, while K93600 alloy belongs to the iron alloys. There are 14 material properties with values for both materials. Properties with values for just one material (18, in this case) are not shown.
For each property being compared, the top bar is C23400 brass and the bottom bar is K93600 alloy.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 140 |
| Tensile Strength: Ultimate (UTS), MPa | 370 to 640 | |
| 480 to 810 |
Thermal Properties
| Maximum Temperature: Mechanical, °C | 160 | |
| 440 |
| Melting Onset (Solidus), °C | 930 | |
| 1430 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 520 |
| Thermal Conductivity, W/m-K | 120 | |
| 13 |
| Thermal Expansion, µm/m-K | 19 | |
| 7.3 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.5 | |
| 8.1 |
Common Calculations
| Stiffness to Weight: Axial, points | 7.2 | |
| 9.4 |
| Stiffness to Weight: Bending, points | 19 | |
| 21 |
| Strength to Weight: Axial, points | 12 to 21 | |
| 16 to 28 |
| Strength to Weight: Bending, points | 13 to 19 | |
| 17 to 24 |
| Thermal Diffusivity, mm2/s | 36 | |
| 3.1 |
| Thermal Shock Resistance, points | 12 to 22 | |
| 34 to 57 |