C24000 Brass vs. C44400 Brass
Both C24000 brass and C44400 brass are copper alloys. They have a moderately high 92% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is C24000 brass and the bottom bar is C44400 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 110 |
| Poisson's Ratio | 0.32 | |
| 0.32 |
| Shear Modulus, GPa | 42 | |
| 41 |
| Tensile Strength: Ultimate (UTS), MPa | 310 to 640 | |
| 350 |
Thermal Properties
| Latent Heat of Fusion, J/g | 190 | |
| 180 |
| Maximum Temperature: Mechanical, °C | 160 | |
| 140 |
| Melting Completion (Liquidus), °C | 1000 | |
| 940 |
| Melting Onset (Solidus), °C | 970 | |
| 900 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 380 |
| Thermal Conductivity, W/m-K | 140 | |
| 110 |
| Thermal Expansion, µm/m-K | 19 | |
| 20 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 32 | |
| 25 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 34 | |
| 27 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 27 | |
| 26 |
| Density, g/cm3 | 8.5 | |
| 8.3 |
| Embodied Carbon, kg CO2/kg material | 2.6 | |
| 2.8 |
| Embodied Energy, MJ/kg | 43 | |
| 46 |
| Embodied Water, L/kg | 320 | |
| 330 |
Common Calculations
| Stiffness to Weight: Axial, points | 7.2 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 19 | |
| 19 |
| Strength to Weight: Axial, points | 10 to 21 | |
| 12 |
| Strength to Weight: Bending, points | 12 to 20 | |
| 13 |
| Thermal Diffusivity, mm2/s | 43 | |
| 35 |
| Thermal Shock Resistance, points | 10 to 22 | |
| 12 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Antimony (Sb), % | 0 | |
| 0.020 to 0.1 |
| Copper (Cu), % | 78.5 to 81.5 | |
| 70 to 73 |
| Iron (Fe), % | 0 to 0.050 | |
| 0 to 0.060 |
| Lead (Pb), % | 0 to 0.050 | |
| 0 to 0.070 |
| Tin (Sn), % | 0 | |
| 0.9 to 1.2 |
| Zinc (Zn), % | 18.2 to 21.5 | |
| 25.2 to 29.1 |
| Residuals, % | 0 to 0.2 | |
| 0 to 0.4 |