C24000 Brass vs. R60804 Alloy
C24000 brass belongs to the copper alloys classification, while R60804 alloy belongs to the otherwise unclassified metals. There are 16 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.
For each property being compared, the top bar is C24000 brass and the bottom bar is R60804 alloy.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 98 |
| Poisson's Ratio | 0.32 | |
| 0.34 |
| Shear Modulus, GPa | 42 | |
| 36 |
| Tensile Strength: Ultimate (UTS), MPa | 310 to 640 | |
| 430 |
Thermal Properties
| Latent Heat of Fusion, J/g | 190 | |
| 250 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 270 |
| Thermal Conductivity, W/m-K | 140 | |
| 22 |
| Thermal Expansion, µm/m-K | 19 | |
| 6.0 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.5 | |
| 6.5 |
| Embodied Water, L/kg | 320 | |
| 290 |
Common Calculations
| Stiffness to Weight: Axial, points | 7.2 | |
| 8.3 |
| Stiffness to Weight: Bending, points | 19 | |
| 23 |
| Strength to Weight: Axial, points | 10 to 21 | |
| 18 |
| Strength to Weight: Bending, points | 12 to 20 | |
| 19 |
| Thermal Diffusivity, mm2/s | 43 | |
| 12 |
| Thermal Shock Resistance, points | 10 to 22 | |
| 53 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Chromium (Cr), % | 0 | |
| 0.070 to 0.13 |
| Copper (Cu), % | 78.5 to 81.5 | |
| 0 |
| Iron (Fe), % | 0 to 0.050 | |
| 0.18 to 0.24 |
| Lead (Pb), % | 0 to 0.050 | |
| 0 |
| Tin (Sn), % | 0 | |
| 1.2 to 1.7 |
| Zinc (Zn), % | 18.2 to 21.5 | |
| 0 |
| Zirconium (Zr), % | 0 | |
| 97.8 to 98.6 |
| Residuals, % | 0 to 0.2 | |
| 0 to 0.12 |