C26800 Brass vs. Commercially Pure Silver
C26800 brass belongs to the copper alloys classification, while commercially pure silver belongs to the otherwise unclassified metals. There are 19 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is C26800 brass and the bottom bar is commercially pure silver.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 71 |
| Poisson's Ratio | 0.31 | |
| 0.37 |
| Shear Modulus, GPa | 40 | |
| 26 |
| Tensile Strength: Ultimate (UTS), MPa | 310 to 650 | |
| 190 to 340 |
Thermal Properties
| Latent Heat of Fusion, J/g | 180 | |
| 110 |
| Melting Completion (Liquidus), °C | 930 | |
| 960 |
| Melting Onset (Solidus), °C | 900 | |
| 960 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 240 |
| Thermal Conductivity, W/m-K | 120 | |
| 420 |
| Thermal Expansion, µm/m-K | 20 | |
| 20 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 27 | |
| 100 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 30 | |
| 87 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.1 | |
| 10 |
Common Calculations
| Stiffness to Weight: Axial, points | 7.2 | |
| 3.8 |
| Stiffness to Weight: Bending, points | 19 | |
| 13 |
| Strength to Weight: Axial, points | 11 to 22 | |
| 4.9 to 8.9 |
| Strength to Weight: Bending, points | 13 to 21 | |
| 6.9 to 10 |
| Thermal Diffusivity, mm2/s | 37 | |
| 170 |
| Thermal Shock Resistance, points | 10 to 22 | |
| 9.5 to 17 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Copper (Cu), % | 64 to 68.5 | |
| 0 |
| Iron (Fe), % | 0 to 0.050 | |
| 0 |
| Lead (Pb), % | 0 to 0.15 | |
| 0 |
| Silver (Ag), % | 0 | |
| 99.9 to 100 |
| Zinc (Zn), % | 31 to 36 | |
| 0 |
| Residuals, % | 0 to 0.3 | |
| 0 to 0.1 |