C27200 Brass vs. C85200 Brass
Both C27200 brass and C85200 brass are copper alloys. They have 87% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is C27200 brass and the bottom bar is C85200 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 110 |
| Elongation at Break, % | 10 to 50 | |
| 28 |
| Poisson's Ratio | 0.31 | |
| 0.32 |
| Shear Modulus, GPa | 40 | |
| 40 |
| Tensile Strength: Ultimate (UTS), MPa | 370 to 590 | |
| 270 |
| Tensile Strength: Yield (Proof), MPa | 150 to 410 | |
| 95 |
Thermal Properties
| Latent Heat of Fusion, J/g | 170 | |
| 180 |
| Maximum Temperature: Mechanical, °C | 130 | |
| 140 |
| Melting Completion (Liquidus), °C | 920 | |
| 940 |
| Melting Onset (Solidus), °C | 870 | |
| 930 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 380 |
| Thermal Conductivity, W/m-K | 120 | |
| 84 |
| Thermal Expansion, µm/m-K | 20 | |
| 20 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 28 | |
| 18 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 31 | |
| 19 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 24 | |
| 26 |
| Density, g/cm3 | 8.1 | |
| 8.4 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 2.8 |
| Embodied Energy, MJ/kg | 45 | |
| 46 |
| Embodied Water, L/kg | 320 | |
| 330 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 30 to 270 | |
| 59 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 110 to 810 | |
| 42 |
| Stiffness to Weight: Axial, points | 7.2 | |
| 7.0 |
| Stiffness to Weight: Bending, points | 19 | |
| 19 |
| Strength to Weight: Axial, points | 13 to 20 | |
| 8.9 |
| Strength to Weight: Bending, points | 14 to 19 | |
| 11 |
| Thermal Diffusivity, mm2/s | 37 | |
| 27 |
| Thermal Shock Resistance, points | 12 to 20 | |
| 9.3 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 | |
| 0 to 0.0050 |
| Antimony (Sb), % | 0 | |
| 0 to 0.2 |
| Copper (Cu), % | 62 to 65 | |
| 70 to 74 |
| Iron (Fe), % | 0 to 0.070 | |
| 0 to 0.6 |
| Lead (Pb), % | 0 to 0.070 | |
| 1.5 to 3.8 |
| Nickel (Ni), % | 0 | |
| 0 to 1.0 |
| Phosphorus (P), % | 0 | |
| 0 to 0.020 |
| Silicon (Si), % | 0 | |
| 0 to 0.050 |
| Sulfur (S), % | 0 | |
| 0 to 0.050 |
| Tin (Sn), % | 0 | |
| 0.7 to 2.0 |
| Zinc (Zn), % | 34.6 to 38 | |
| 20 to 27 |
| Residuals, % | 0 to 0.3 | |
| 0 to 0.9 |