C31400 Bronze vs. C11400 Copper

Both C31400 bronze and C11400 copper are copper alloys. They have 89% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is C31400 bronze and the bottom bar is C11400 copper.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
120
Elongation at Break, % 6.8 to 29
2.8 to 51
Poisson's Ratio 0.33
0.34
Shear Modulus, GPa 42
43
Shear Strength, MPa 180 to 240
150 to 210
Tensile Strength: Ultimate (UTS), MPa 270 to 420
220 to 400
Tensile Strength: Yield (Proof), MPa 78 to 310
75 to 400

Thermal Properties

Latent Heat of Fusion, J/g 200
210
Maximum Temperature: Mechanical, °C 180
200
Melting Completion (Liquidus), °C 1040
1080
Melting Onset (Solidus), °C 1010
1030
Specific Heat Capacity, J/kg-K 380
390
Thermal Conductivity, W/m-K 180
390
Thermal Expansion, µm/m-K 18
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 42
100
Electrical Conductivity: Equal Weight (Specific), % IACS 43
100

Otherwise Unclassified Properties

Base Metal Price, % relative 29
32
Density, g/cm3 8.8
9.0
Embodied Carbon, kg CO2/kg material 2.6
2.6
Embodied Energy, MJ/kg 42
42
Embodied Water, L/kg 310
350

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 26 to 59
11 to 90
Resilience: Unit (Modulus of Resilience), kJ/m3 28 to 420
24 to 680
Stiffness to Weight: Axial, points 7.1
7.2
Stiffness to Weight: Bending, points 18
18
Strength to Weight: Axial, points 8.7 to 13
6.8 to 12
Strength to Weight: Bending, points 11 to 14
9.1 to 14
Thermal Diffusivity, mm2/s 54
110
Thermal Shock Resistance, points 9.6 to 15
7.8 to 14

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Copper (Cu), % 87.5 to 90.5
99.84 to 99.966
Iron (Fe), % 0 to 0.1
0
Lead (Pb), % 1.3 to 2.5
0
Nickel (Ni), % 0 to 0.7
0
Silver (Ag), % 0
0.034 to 0.060
Zinc (Zn), % 5.8 to 11.2
0
Residuals, % 0 to 0.4
0 to 0.1

Comparable Variants