C31400 Bronze vs. C27200 Brass

Both C31400 bronze and C27200 brass are copper alloys. They have 72% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is C31400 bronze and the bottom bar is C27200 brass.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
110
Elongation at Break, % 6.8 to 29
10 to 50
Poisson's Ratio 0.33
0.31
Shear Modulus, GPa 42
40
Shear Strength, MPa 180 to 240
230 to 320
Tensile Strength: Ultimate (UTS), MPa 270 to 420
370 to 590
Tensile Strength: Yield (Proof), MPa 78 to 310
150 to 410

Thermal Properties

Latent Heat of Fusion, J/g 200
170
Maximum Temperature: Mechanical, °C 180
130
Melting Completion (Liquidus), °C 1040
920
Melting Onset (Solidus), °C 1010
870
Specific Heat Capacity, J/kg-K 380
390
Thermal Conductivity, W/m-K 180
120
Thermal Expansion, µm/m-K 18
20

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 42
28
Electrical Conductivity: Equal Weight (Specific), % IACS 43
31

Otherwise Unclassified Properties

Base Metal Price, % relative 29
24
Density, g/cm3 8.8
8.1
Embodied Carbon, kg CO2/kg material 2.6
2.7
Embodied Energy, MJ/kg 42
45
Embodied Water, L/kg 310
320

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 26 to 59
30 to 270
Resilience: Unit (Modulus of Resilience), kJ/m3 28 to 420
110 to 810
Stiffness to Weight: Axial, points 7.1
7.2
Stiffness to Weight: Bending, points 18
19
Strength to Weight: Axial, points 8.7 to 13
13 to 20
Strength to Weight: Bending, points 11 to 14
14 to 19
Thermal Diffusivity, mm2/s 54
37
Thermal Shock Resistance, points 9.6 to 15
12 to 20

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Copper (Cu), % 87.5 to 90.5
62 to 65
Iron (Fe), % 0 to 0.1
0 to 0.070
Lead (Pb), % 1.3 to 2.5
0 to 0.070
Nickel (Ni), % 0 to 0.7
0
Zinc (Zn), % 5.8 to 11.2
34.6 to 38
Residuals, % 0 to 0.4
0 to 0.3

Comparable Variants