C33200 Brass vs. C14700 Copper
Both C33200 brass and C14700 copper are copper alloys. They have 67% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is C33200 brass and the bottom bar is C14700 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 120 |
| Elongation at Break, % | 7.0 to 60 | |
| 9.1 to 35 |
| Poisson's Ratio | 0.31 | |
| 0.34 |
| Shear Modulus, GPa | 40 | |
| 43 |
| Shear Strength, MPa | 240 to 300 | |
| 160 to 190 |
| Tensile Strength: Ultimate (UTS), MPa | 320 to 520 | |
| 240 to 320 |
| Tensile Strength: Yield (Proof), MPa | 110 to 450 | |
| 85 to 250 |
Thermal Properties
| Latent Heat of Fusion, J/g | 170 | |
| 210 |
| Maximum Temperature: Mechanical, °C | 130 | |
| 200 |
| Melting Completion (Liquidus), °C | 930 | |
| 1080 |
| Melting Onset (Solidus), °C | 900 | |
| 1070 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 390 |
| Thermal Conductivity, W/m-K | 120 | |
| 370 |
| Thermal Expansion, µm/m-K | 20 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 26 | |
| 95 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 28 | |
| 96 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 24 | |
| 30 |
| Density, g/cm3 | 8.2 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 2.6 | |
| 2.6 |
| Embodied Energy, MJ/kg | 44 | |
| 41 |
| Embodied Water, L/kg | 320 | |
| 310 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 35 to 150 | |
| 25 to 65 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 60 to 960 | |
| 31 to 280 |
| Stiffness to Weight: Axial, points | 7.1 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 19 | |
| 18 |
| Strength to Weight: Axial, points | 11 to 17 | |
| 7.3 to 10 |
| Strength to Weight: Bending, points | 13 to 17 | |
| 9.5 to 12 |
| Thermal Diffusivity, mm2/s | 37 | |
| 110 |
| Thermal Shock Resistance, points | 11 to 17 | |
| 8.4 to 12 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Copper (Cu), % | 65 to 68 | |
| 99.395 to 99.798 |
| Iron (Fe), % | 0 to 0.070 | |
| 0 |
| Lead (Pb), % | 1.5 to 2.5 | |
| 0 |
| Phosphorus (P), % | 0 | |
| 0.0020 to 0.0050 |
| Sulfur (S), % | 0 | |
| 0.2 to 0.5 |
| Zinc (Zn), % | 29 to 33.5 | |
| 0 |
| Residuals, % | 0 to 0.4 | |
| 0 to 0.1 |