MakeItFrom.com
Menu (ESC)

C35000 Brass vs. EN 1.4110 Stainless Steel

C35000 brass belongs to the copper alloys classification, while EN 1.4110 stainless steel belongs to the iron alloys. There are 24 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is C35000 brass and the bottom bar is EN 1.4110 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 100
190
Poisson's Ratio 0.31
0.28
Shear Modulus, GPa 40
76
Tensile Strength: Ultimate (UTS), MPa 340 to 650
770 to 1720

Thermal Properties

Latent Heat of Fusion, J/g 170
280
Maximum Temperature: Mechanical, °C 120
790
Melting Completion (Liquidus), °C 920
1440
Melting Onset (Solidus), °C 890
1400
Specific Heat Capacity, J/kg-K 380
480
Thermal Conductivity, W/m-K 120
30
Thermal Expansion, µm/m-K 21
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 26
2.8
Electrical Conductivity: Equal Weight (Specific), % IACS 29
3.2

Otherwise Unclassified Properties

Base Metal Price, % relative 23
8.0
Density, g/cm3 8.1
7.7
Embodied Carbon, kg CO2/kg material 2.7
2.3
Embodied Energy, MJ/kg 45
33
Embodied Water, L/kg 320
110

Common Calculations

Stiffness to Weight: Axial, points 7.1
14
Stiffness to Weight: Bending, points 19
25
Strength to Weight: Axial, points 12 to 22
28 to 62
Strength to Weight: Bending, points 13 to 21
24 to 41
Thermal Diffusivity, mm2/s 37
8.1
Thermal Shock Resistance, points 11 to 22
27 to 60

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0
0.48 to 0.6
Chromium (Cr), % 0
13 to 15
Copper (Cu), % 60 to 63
0
Iron (Fe), % 0 to 0.1
81.4 to 86
Lead (Pb), % 0.8 to 2.0
0
Manganese (Mn), % 0
0 to 1.0
Molybdenum (Mo), % 0
0.5 to 0.8
Phosphorus (P), % 0
0 to 0.040
Silicon (Si), % 0
0 to 1.0
Sulfur (S), % 0
0 to 0.015
Vanadium (V), % 0
0 to 0.15
Zinc (Zn), % 34.5 to 39.2
0
Residuals, % 0 to 0.4
0