C35000 Brass vs. EN 1.4530 Stainless Steel

C35000 brass belongs to the copper alloys classification, while EN 1.4530 stainless steel belongs to the iron alloys. There are 20 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is C35000 brass and the bottom bar is EN 1.4530 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 100
200
Poisson's Ratio 0.31
0.28
Shear Modulus, GPa 40
76
Tensile Strength: Ultimate (UTS), MPa 340 to 650
1030 to 1370

Thermal Properties

Latent Heat of Fusion, J/g 170
270
Maximum Temperature: Mechanical, °C 120
790
Melting Completion (Liquidus), °C 920
1460
Melting Onset (Solidus), °C 890
1410
Specific Heat Capacity, J/kg-K 380
470
Thermal Expansion, µm/m-K 21
11

Otherwise Unclassified Properties

Base Metal Price, % relative 23
15
Density, g/cm3 8.1
7.9
Embodied Carbon, kg CO2/kg material 2.7
3.4
Embodied Energy, MJ/kg 45
46
Embodied Water, L/kg 320
130

Common Calculations

Stiffness to Weight: Axial, points 7.1
14
Stiffness to Weight: Bending, points 19
25
Strength to Weight: Axial, points 12 to 22
36 to 48
Strength to Weight: Bending, points 13 to 21
29 to 35
Thermal Shock Resistance, points 11 to 22
35 to 47

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0
0.6 to 0.8
Carbon (C), % 0
0 to 0.015
Chromium (Cr), % 0
11.5 to 12.5
Copper (Cu), % 60 to 63
0
Iron (Fe), % 0 to 0.1
74.4 to 77.3
Lead (Pb), % 0.8 to 2.0
0
Manganese (Mn), % 0
0 to 0.1
Molybdenum (Mo), % 0
1.9 to 2.2
Nickel (Ni), % 0
8.5 to 9.5
Nitrogen (N), % 0
0 to 0.010
Phosphorus (P), % 0
0 to 0.010
Silicon (Si), % 0
0 to 0.1
Sulfur (S), % 0
0 to 0.0050
Titanium (Ti), % 0
0.28 to 0.37
Zinc (Zn), % 34.5 to 39.2
0
Residuals, % 0 to 0.4
0