C35600 Brass vs. AWS ERNiCrMo-3

C35600 brass belongs to the copper alloys classification, while AWS ERNiCrMo-3 belongs to the nickel alloys. There are 23 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is C35600 brass and the bottom bar is AWS ERNiCrMo-3.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 100
200
Poisson's Ratio 0.31
0.29
Shear Modulus, GPa 39
79
Tensile Strength: Ultimate (UTS), MPa 340 to 650
870

Thermal Properties

Latent Heat of Fusion, J/g 170
330
Melting Completion (Liquidus), °C 900
1480
Melting Onset (Solidus), °C 890
1430
Specific Heat Capacity, J/kg-K 380
440
Thermal Conductivity, W/m-K 120
11
Thermal Expansion, µm/m-K 21
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 26
1.3
Electrical Conductivity: Equal Weight (Specific), % IACS 29
1.4

Otherwise Unclassified Properties

Base Metal Price, % relative 23
80
Density, g/cm3 8.1
8.6
Embodied Carbon, kg CO2/kg material 2.6
14
Embodied Energy, MJ/kg 45
190
Embodied Water, L/kg 320
290

Common Calculations

Stiffness to Weight: Axial, points 7.0
13
Stiffness to Weight: Bending, points 19
23
Strength to Weight: Axial, points 11 to 22
28
Strength to Weight: Bending, points 13 to 21
24
Thermal Diffusivity, mm2/s 38
2.8
Thermal Shock Resistance, points 11 to 22
25

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0
0 to 0.4
Carbon (C), % 0
0 to 0.010
Chromium (Cr), % 0
20 to 23
Copper (Cu), % 60 to 63
0 to 0.5
Iron (Fe), % 0 to 0.1
0 to 5.0
Lead (Pb), % 2.0 to 3.0
0
Manganese (Mn), % 0
0 to 0.5
Molybdenum (Mo), % 0
8.0 to 10
Nickel (Ni), % 0
58 to 68.9
Niobium (Nb), % 0
3.2 to 4.2
Phosphorus (P), % 0
0 to 0.020
Silicon (Si), % 0
0 to 0.5
Sulfur (S), % 0
0 to 0.015
Titanium (Ti), % 0
0 to 0.4
Zinc (Zn), % 33.4 to 38
0
Residuals, % 0 to 0.5
0 to 0.5