C35600 Brass vs. C96900 Copper-nickel
Both C35600 brass and C96900 copper-nickel are copper alloys. They have 62% of their average alloy composition in common. There are 22 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is C35600 brass and the bottom bar is C96900 copper-nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 120 |
| Poisson's Ratio | 0.31 | |
| 0.34 |
| Shear Modulus, GPa | 39 | |
| 45 |
| Tensile Strength: Ultimate (UTS), MPa | 340 to 650 | |
| 850 |
Thermal Properties
| Latent Heat of Fusion, J/g | 170 | |
| 210 |
| Maximum Temperature: Mechanical, °C | 120 | |
| 210 |
| Melting Completion (Liquidus), °C | 900 | |
| 1060 |
| Melting Onset (Solidus), °C | 890 | |
| 960 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 380 |
| Thermal Expansion, µm/m-K | 21 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 26 | |
| 9.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 29 | |
| 9.2 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 23 | |
| 39 |
| Density, g/cm3 | 8.1 | |
| 8.8 |
| Embodied Carbon, kg CO2/kg material | 2.6 | |
| 4.6 |
| Embodied Energy, MJ/kg | 45 | |
| 72 |
| Embodied Water, L/kg | 320 | |
| 360 |
Common Calculations
| Stiffness to Weight: Axial, points | 7.0 | |
| 7.7 |
| Stiffness to Weight: Bending, points | 19 | |
| 19 |
| Strength to Weight: Axial, points | 11 to 22 | |
| 27 |
| Strength to Weight: Bending, points | 13 to 21 | |
| 23 |
| Thermal Shock Resistance, points | 11 to 22 | |
| 30 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Copper (Cu), % | 60 to 63 | |
| 73.6 to 78 |
| Iron (Fe), % | 0 to 0.1 | |
| 0 to 0.5 |
| Lead (Pb), % | 2.0 to 3.0 | |
| 0 to 0.020 |
| Magnesium (Mg), % | 0 | |
| 0 to 0.15 |
| Manganese (Mn), % | 0 | |
| 0.050 to 0.3 |
| Nickel (Ni), % | 0 | |
| 14.5 to 15.5 |
| Niobium (Nb), % | 0 | |
| 0 to 0.1 |
| Silicon (Si), % | 0 | |
| 0 to 0.3 |
| Tin (Sn), % | 0 | |
| 7.5 to 8.5 |
| Zinc (Zn), % | 33.4 to 38 | |
| 0 to 0.5 |
| Residuals, % | 0 to 0.5 | |
| 0 to 0.5 |