C35600 Brass vs. N10675 Nickel

C35600 brass belongs to the copper alloys classification, while N10675 nickel belongs to the nickel alloys. There are 25 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is C35600 brass and the bottom bar is N10675 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 100
220
Poisson's Ratio 0.31
0.31
Rockwell B Hardness 53 to 91
88
Shear Modulus, GPa 39
85
Tensile Strength: Ultimate (UTS), MPa 340 to 650
860

Thermal Properties

Latent Heat of Fusion, J/g 170
320
Maximum Temperature: Mechanical, °C 120
910
Melting Completion (Liquidus), °C 900
1420
Melting Onset (Solidus), °C 890
1370
Specific Heat Capacity, J/kg-K 380
380
Thermal Conductivity, W/m-K 120
11
Thermal Expansion, µm/m-K 21
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 26
1.3
Electrical Conductivity: Equal Weight (Specific), % IACS 29
1.2

Otherwise Unclassified Properties

Base Metal Price, % relative 23
80
Density, g/cm3 8.1
9.3
Embodied Carbon, kg CO2/kg material 2.6
16
Embodied Energy, MJ/kg 45
210
Embodied Water, L/kg 320
280

Common Calculations

Stiffness to Weight: Axial, points 7.0
13
Stiffness to Weight: Bending, points 19
22
Strength to Weight: Axial, points 11 to 22
26
Strength to Weight: Bending, points 13 to 21
22
Thermal Diffusivity, mm2/s 38
3.1
Thermal Shock Resistance, points 11 to 22
26

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0
0 to 0.5
Carbon (C), % 0
0 to 0.010
Chromium (Cr), % 0
1.0 to 3.0
Cobalt (Co), % 0
0 to 3.0
Copper (Cu), % 60 to 63
0 to 0.2
Iron (Fe), % 0 to 0.1
1.0 to 3.0
Lead (Pb), % 2.0 to 3.0
0
Manganese (Mn), % 0
0 to 3.0
Molybdenum (Mo), % 0
27 to 32
Nickel (Ni), % 0
51.3 to 71
Niobium (Nb), % 0
0 to 0.2
Phosphorus (P), % 0
0 to 0.030
Silicon (Si), % 0
0 to 0.1
Sulfur (S), % 0
0 to 0.010
Tantalum (Ta), % 0
0 to 0.2
Titanium (Ti), % 0
0 to 0.2
Tungsten (W), % 0
0 to 3.0
Vanadium (V), % 0
0 to 0.2
Zinc (Zn), % 33.4 to 38
0 to 0.1
Residuals, % 0 to 0.5
0