C36000 Brass vs. SAE-AISI H22 Steel
C36000 brass belongs to the copper alloys classification, while SAE-AISI H22 steel belongs to the iron alloys. There are 21 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is C36000 brass and the bottom bar is SAE-AISI H22 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 200 |
| Poisson's Ratio | 0.31 | |
| 0.29 |
| Shear Modulus, GPa | 39 | |
| 77 |
| Tensile Strength: Ultimate (UTS), MPa | 330 to 530 | |
| 700 to 1920 |
Thermal Properties
| Latent Heat of Fusion, J/g | 170 | |
| 250 |
| Melting Completion (Liquidus), °C | 900 | |
| 1670 |
| Melting Onset (Solidus), °C | 890 | |
| 1620 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 440 |
| Thermal Conductivity, W/m-K | 120 | |
| 31 |
| Thermal Expansion, µm/m-K | 21 | |
| 12 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 23 | |
| 28 |
| Density, g/cm3 | 8.2 | |
| 8.7 |
| Embodied Carbon, kg CO2/kg material | 2.6 | |
| 4.9 |
| Embodied Energy, MJ/kg | 45 | |
| 73 |
| Embodied Water, L/kg | 320 | |
| 72 |
Common Calculations
| Stiffness to Weight: Axial, points | 7.0 | |
| 13 |
| Stiffness to Weight: Bending, points | 19 | |
| 22 |
| Strength to Weight: Axial, points | 11 to 18 | |
| 22 to 61 |
| Strength to Weight: Bending, points | 13 to 18 | |
| 20 to 39 |
| Thermal Diffusivity, mm2/s | 37 | |
| 8.2 |
| Thermal Shock Resistance, points | 11 to 18 | |
| 22 to 60 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Carbon (C), % | 0 | |
| 0.3 to 0.4 |
| Chromium (Cr), % | 0 | |
| 1.8 to 3.8 |
| Copper (Cu), % | 60 to 63 | |
| 0 to 0.25 |
| Iron (Fe), % | 0 to 0.35 | |
| 82.2 to 87.4 |
| Lead (Pb), % | 2.5 to 3.7 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 0.15 to 0.4 |
| Nickel (Ni), % | 0 | |
| 0 to 0.3 |
| Phosphorus (P), % | 0 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 | |
| 0.15 to 0.4 |
| Sulfur (S), % | 0 | |
| 0 to 0.030 |
| Tungsten (W), % | 0 | |
| 10 to 11.8 |
| Vanadium (V), % | 0 | |
| 0.25 to 0.5 |
| Zinc (Zn), % | 32.5 to 37.5 | |
| 0 |
| Residuals, % | 0 to 0.5 | |
| 0 |