C38000 Brass vs. C49300 Brass
Both C38000 brass and C49300 brass are copper alloys. They have a moderately high 94% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is C38000 brass and the bottom bar is C49300 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 100 |
| Elongation at Break, % | 17 | |
| 4.5 to 20 |
| Poisson's Ratio | 0.31 | |
| 0.31 |
| Shear Modulus, GPa | 39 | |
| 40 |
| Shear Strength, MPa | 230 | |
| 270 to 290 |
| Tensile Strength: Ultimate (UTS), MPa | 380 | |
| 430 to 520 |
| Tensile Strength: Yield (Proof), MPa | 120 | |
| 210 to 410 |
Thermal Properties
| Latent Heat of Fusion, J/g | 170 | |
| 170 |
| Maximum Temperature: Mechanical, °C | 110 | |
| 120 |
| Melting Completion (Liquidus), °C | 800 | |
| 880 |
| Melting Onset (Solidus), °C | 760 | |
| 840 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 380 |
| Thermal Conductivity, W/m-K | 110 | |
| 88 |
| Thermal Expansion, µm/m-K | 21 | |
| 20 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 22 | |
| 26 |
| Density, g/cm3 | 8.0 | |
| 8.0 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 3.0 |
| Embodied Energy, MJ/kg | 46 | |
| 50 |
| Embodied Water, L/kg | 330 | |
| 370 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 50 | |
| 21 to 71 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 74 | |
| 220 to 800 |
| Stiffness to Weight: Axial, points | 7.1 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 19 | |
| 19 |
| Strength to Weight: Axial, points | 13 | |
| 15 to 18 |
| Strength to Weight: Bending, points | 14 | |
| 16 to 18 |
| Thermal Diffusivity, mm2/s | 37 | |
| 29 |
| Thermal Shock Resistance, points | 13 | |
| 14 to 18 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 to 0.5 | |
| 0 to 0.5 |
| Antimony (Sb), % | 0 | |
| 0 to 0.5 |
| Bismuth (Bi), % | 0 | |
| 0.5 to 2.0 |
| Copper (Cu), % | 55 to 60 | |
| 58 to 62 |
| Iron (Fe), % | 0 to 0.35 | |
| 0 to 0.1 |
| Lead (Pb), % | 1.5 to 2.5 | |
| 0 to 0.010 |
| Manganese (Mn), % | 0 | |
| 0 to 0.030 |
| Nickel (Ni), % | 0 | |
| 0 to 1.5 |
| Phosphorus (P), % | 0 | |
| 0 to 0.2 |
| Selenium (Se), % | 0 | |
| 0 to 0.2 |
| Silicon (Si), % | 0 | |
| 0 to 0.1 |
| Tin (Sn), % | 0 to 0.3 | |
| 1.0 to 1.8 |
| Zinc (Zn), % | 35.9 to 43.5 | |
| 30.6 to 40.5 |
| Residuals, % | 0 to 0.5 | |
| 0 to 0.5 |