C38500 Bronze vs. SAE-AISI 1080 Steel
C38500 bronze belongs to the copper alloys classification, while SAE-AISI 1080 steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is C38500 bronze and the bottom bar is SAE-AISI 1080 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 190 |
| Elongation at Break, % | 17 | |
| 11 |
| Poisson's Ratio | 0.31 | |
| 0.29 |
| Shear Modulus, GPa | 37 | |
| 72 |
| Shear Strength, MPa | 230 | |
| 460 to 520 |
| Tensile Strength: Ultimate (UTS), MPa | 370 | |
| 770 to 870 |
| Tensile Strength: Yield (Proof), MPa | 130 | |
| 480 to 590 |
Thermal Properties
| Latent Heat of Fusion, J/g | 160 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 110 | |
| 400 |
| Melting Completion (Liquidus), °C | 890 | |
| 1450 |
| Melting Onset (Solidus), °C | 880 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 470 |
| Thermal Conductivity, W/m-K | 120 | |
| 51 |
| Thermal Expansion, µm/m-K | 21 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 28 | |
| 9.6 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 31 | |
| 11 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 22 | |
| 1.8 |
| Density, g/cm3 | 8.1 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 2.6 | |
| 1.4 |
| Embodied Energy, MJ/kg | 45 | |
| 19 |
| Embodied Water, L/kg | 320 | |
| 46 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 48 | |
| 80 to 84 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 78 | |
| 610 to 920 |
| Stiffness to Weight: Axial, points | 7.0 | |
| 13 |
| Stiffness to Weight: Bending, points | 19 | |
| 24 |
| Strength to Weight: Axial, points | 13 | |
| 27 to 31 |
| Strength to Weight: Bending, points | 14 | |
| 24 to 26 |
| Thermal Diffusivity, mm2/s | 40 | |
| 14 |
| Thermal Shock Resistance, points | 12 | |
| 25 to 29 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Carbon (C), % | 0 | |
| 0.75 to 0.88 |
| Copper (Cu), % | 55 to 59 | |
| 0 |
| Iron (Fe), % | 0 to 0.35 | |
| 98.1 to 98.7 |
| Lead (Pb), % | 2.5 to 3.5 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 0.6 to 0.9 |
| Phosphorus (P), % | 0 | |
| 0 to 0.040 |
| Sulfur (S), % | 0 | |
| 0 to 0.050 |
| Zinc (Zn), % | 36.7 to 42.5 | |
| 0 |
| Residuals, % | 0 to 0.5 | |
| 0 |