C40500 Penny Bronze vs. C12200 Copper
Both C40500 penny bronze and C12200 copper are copper alloys. They have a very high 95% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is C40500 penny bronze and the bottom bar is C12200 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 120 |
| Elongation at Break, % | 3.0 to 49 | |
| 3.2 to 50 |
| Poisson's Ratio | 0.34 | |
| 0.34 |
| Rockwell Superficial 30T Hardness | 10 to 72 | |
| 27 to 70 |
| Shear Modulus, GPa | 43 | |
| 43 |
| Shear Strength, MPa | 210 to 310 | |
| 150 to 240 |
| Tensile Strength: Ultimate (UTS), MPa | 270 to 540 | |
| 220 to 410 |
| Tensile Strength: Yield (Proof), MPa | 79 to 520 | |
| 69 to 400 |
Thermal Properties
| Latent Heat of Fusion, J/g | 200 | |
| 210 |
| Maximum Temperature: Mechanical, °C | 190 | |
| 200 |
| Melting Completion (Liquidus), °C | 1060 | |
| 1080 |
| Melting Onset (Solidus), °C | 1020 | |
| 1030 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 390 |
| Thermal Conductivity, W/m-K | 160 | |
| 340 |
| Thermal Expansion, µm/m-K | 18 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 41 | |
| 85 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 42 | |
| 85 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 30 | |
| 31 |
| Density, g/cm3 | 8.8 | |
| 9.0 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 2.6 |
| Embodied Energy, MJ/kg | 43 | |
| 41 |
| Embodied Water, L/kg | 320 | |
| 310 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 16 to 110 | |
| 11 to 91 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 28 to 1200 | |
| 21 to 690 |
| Stiffness to Weight: Axial, points | 7.2 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 18 | |
| 18 |
| Strength to Weight: Axial, points | 8.5 to 17 | |
| 6.9 to 13 |
| Strength to Weight: Bending, points | 10 to 17 | |
| 9.1 to 14 |
| Thermal Diffusivity, mm2/s | 48 | |
| 98 |
| Thermal Shock Resistance, points | 9.5 to 19 | |
| 7.9 to 15 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Copper (Cu), % | 94 to 96 | |
| 99.9 to 99.985 |
| Iron (Fe), % | 0 to 0.050 | |
| 0 |
| Lead (Pb), % | 0 to 0.050 | |
| 0 |
| Phosphorus (P), % | 0 | |
| 0.015 to 0.040 |
| Tin (Sn), % | 0.7 to 1.3 | |
| 0 |
| Zinc (Zn), % | 2.1 to 5.3 | |
| 0 |
| Residuals, % | 0 to 0.5 | |
| 0 |