C41300 Brass vs. EN 1.1170 Steel
C41300 brass belongs to the copper alloys classification, while EN 1.1170 steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is C41300 brass and the bottom bar is EN 1.1170 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 190 |
| Elongation at Break, % | 2.0 to 44 | |
| 16 to 17 |
| Poisson's Ratio | 0.33 | |
| 0.29 |
| Shear Modulus, GPa | 42 | |
| 73 |
| Shear Strength, MPa | 230 to 370 | |
| 390 to 450 |
| Tensile Strength: Ultimate (UTS), MPa | 300 to 630 | |
| 640 to 730 |
| Tensile Strength: Yield (Proof), MPa | 120 to 570 | |
| 330 to 500 |
Thermal Properties
| Latent Heat of Fusion, J/g | 200 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 180 | |
| 400 |
| Melting Completion (Liquidus), °C | 1040 | |
| 1460 |
| Melting Onset (Solidus), °C | 1010 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 470 |
| Thermal Conductivity, W/m-K | 130 | |
| 50 |
| Thermal Expansion, µm/m-K | 18 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 30 | |
| 7.3 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 31 | |
| 8.4 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 29 | |
| 2.1 |
| Density, g/cm3 | 8.7 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 1.5 |
| Embodied Energy, MJ/kg | 44 | |
| 19 |
| Embodied Water, L/kg | 320 | |
| 49 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 11 to 110 | |
| 91 to 100 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 69 to 1440 | |
| 290 to 670 |
| Stiffness to Weight: Axial, points | 7.2 | |
| 13 |
| Stiffness to Weight: Bending, points | 18 | |
| 24 |
| Strength to Weight: Axial, points | 9.6 to 20 | |
| 23 to 26 |
| Strength to Weight: Bending, points | 11 to 19 | |
| 21 to 23 |
| Thermal Diffusivity, mm2/s | 40 | |
| 13 |
| Thermal Shock Resistance, points | 11 to 22 | |
| 20 to 23 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Carbon (C), % | 0 | |
| 0.25 to 0.32 |
| Chromium (Cr), % | 0 | |
| 0 to 0.4 |
| Copper (Cu), % | 89 to 93 | |
| 0 |
| Iron (Fe), % | 0 to 0.050 | |
| 96.7 to 98.5 |
| Lead (Pb), % | 0 to 0.1 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 1.3 to 1.7 |
| Molybdenum (Mo), % | 0 | |
| 0 to 0.1 |
| Nickel (Ni), % | 0 | |
| 0 to 0.4 |
| Phosphorus (P), % | 0 | |
| 0 to 0.035 |
| Silicon (Si), % | 0 | |
| 0 to 0.4 |
| Sulfur (S), % | 0 | |
| 0 to 0.035 |
| Tin (Sn), % | 0.7 to 1.3 | |
| 0 |
| Zinc (Zn), % | 5.1 to 10.3 | |
| 0 |
| Residuals, % | 0 to 0.5 | |
| 0 |