C41300 Brass vs. C14200 Copper
Both C41300 brass and C14200 copper are copper alloys. They have a moderately high 91% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is C41300 brass and the bottom bar is C14200 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 120 |
| Elongation at Break, % | 2.0 to 44 | |
| 8.0 to 45 |
| Poisson's Ratio | 0.33 | |
| 0.34 |
| Rockwell B Hardness | 53 to 88 | |
| 35 to 60 |
| Rockwell Superficial 30T Hardness | 20 to 77 | |
| 45 to 63 |
| Shear Modulus, GPa | 42 | |
| 43 |
| Shear Strength, MPa | 230 to 370 | |
| 150 to 200 |
| Tensile Strength: Ultimate (UTS), MPa | 300 to 630 | |
| 220 to 370 |
| Tensile Strength: Yield (Proof), MPa | 120 to 570 | |
| 75 to 340 |
Thermal Properties
| Latent Heat of Fusion, J/g | 200 | |
| 210 |
| Maximum Temperature: Mechanical, °C | 180 | |
| 200 |
| Melting Completion (Liquidus), °C | 1040 | |
| 1080 |
| Melting Onset (Solidus), °C | 1010 | |
| 1030 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 390 |
| Thermal Conductivity, W/m-K | 130 | |
| 190 |
| Thermal Expansion, µm/m-K | 18 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 30 | |
| 45 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 31 | |
| 45 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 29 | |
| 31 |
| Density, g/cm3 | 8.7 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 2.6 |
| Embodied Energy, MJ/kg | 44 | |
| 41 |
| Embodied Water, L/kg | 320 | |
| 310 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 11 to 110 | |
| 29 to 83 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 69 to 1440 | |
| 24 to 500 |
| Stiffness to Weight: Axial, points | 7.2 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 18 | |
| 18 |
| Strength to Weight: Axial, points | 9.6 to 20 | |
| 6.8 to 11 |
| Strength to Weight: Bending, points | 11 to 19 | |
| 9.1 to 13 |
| Thermal Diffusivity, mm2/s | 40 | |
| 56 |
| Thermal Shock Resistance, points | 11 to 22 | |
| 7.9 to 13 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Arsenic (As), % | 0 | |
| 0.15 to 0.5 |
| Copper (Cu), % | 89 to 93 | |
| 99.4 to 99.835 |
| Iron (Fe), % | 0 to 0.050 | |
| 0 |
| Lead (Pb), % | 0 to 0.1 | |
| 0 |
| Phosphorus (P), % | 0 | |
| 0.015 to 0.040 |
| Tin (Sn), % | 0.7 to 1.3 | |
| 0 |
| Zinc (Zn), % | 5.1 to 10.3 | |
| 0 |
| Residuals, % | 0 to 0.5 | |
| 0 |