C41300 Brass vs. C68300 Brass
Both C41300 brass and C68300 brass are copper alloys. They have 69% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is C41300 brass and the bottom bar is C68300 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 100 |
| Elongation at Break, % | 2.0 to 44 | |
| 15 |
| Poisson's Ratio | 0.33 | |
| 0.31 |
| Rockwell B Hardness | 53 to 88 | |
| 60 |
| Shear Modulus, GPa | 42 | |
| 40 |
| Shear Strength, MPa | 230 to 370 | |
| 260 |
| Tensile Strength: Ultimate (UTS), MPa | 300 to 630 | |
| 430 |
| Tensile Strength: Yield (Proof), MPa | 120 to 570 | |
| 260 |
Thermal Properties
| Latent Heat of Fusion, J/g | 200 | |
| 180 |
| Maximum Temperature: Mechanical, °C | 180 | |
| 120 |
| Melting Completion (Liquidus), °C | 1040 | |
| 900 |
| Melting Onset (Solidus), °C | 1010 | |
| 890 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 390 |
| Thermal Conductivity, W/m-K | 130 | |
| 120 |
| Thermal Expansion, µm/m-K | 18 | |
| 20 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 29 | |
| 23 |
| Density, g/cm3 | 8.7 | |
| 8.0 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 2.8 |
| Embodied Energy, MJ/kg | 44 | |
| 46 |
| Embodied Water, L/kg | 320 | |
| 340 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 11 to 110 | |
| 56 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 69 to 1440 | |
| 330 |
| Stiffness to Weight: Axial, points | 7.2 | |
| 7.3 |
| Stiffness to Weight: Bending, points | 18 | |
| 20 |
| Strength to Weight: Axial, points | 9.6 to 20 | |
| 15 |
| Strength to Weight: Bending, points | 11 to 19 | |
| 16 |
| Thermal Diffusivity, mm2/s | 40 | |
| 38 |
| Thermal Shock Resistance, points | 11 to 22 | |
| 14 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Antimony (Sb), % | 0 | |
| 0.3 to 1.0 |
| Cadmium (Cd), % | 0 | |
| 0 to 0.010 |
| Copper (Cu), % | 89 to 93 | |
| 59 to 63 |
| Iron (Fe), % | 0 to 0.050 | |
| 0 |
| Lead (Pb), % | 0 to 0.1 | |
| 0 to 0.090 |
| Silicon (Si), % | 0 | |
| 0.3 to 1.0 |
| Tin (Sn), % | 0.7 to 1.3 | |
| 0.050 to 0.2 |
| Zinc (Zn), % | 5.1 to 10.3 | |
| 34.2 to 40.4 |
| Residuals, % | 0 to 0.5 | |
| 0 to 0.5 |