C41500 Brass vs. C10800 Copper
Both C41500 brass and C10800 copper are copper alloys. They have a moderately high 91% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is C41500 brass and the bottom bar is C10800 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 120 |
| Elongation at Break, % | 2.0 to 42 | |
| 4.0 to 50 |
| Poisson's Ratio | 0.33 | |
| 0.34 |
| Rockwell B Hardness | 62 to 90 | |
| 10 to 60 |
| Rockwell Superficial 30T Hardness | 36 to 75 | |
| 27 to 63 |
| Shear Modulus, GPa | 42 | |
| 43 |
| Shear Strength, MPa | 220 to 360 | |
| 150 to 200 |
| Tensile Strength: Ultimate (UTS), MPa | 340 to 560 | |
| 220 to 380 |
| Tensile Strength: Yield (Proof), MPa | 190 to 550 | |
| 75 to 370 |
Thermal Properties
| Latent Heat of Fusion, J/g | 200 | |
| 210 |
| Maximum Temperature: Mechanical, °C | 180 | |
| 200 |
| Melting Completion (Liquidus), °C | 1030 | |
| 1080 |
| Melting Onset (Solidus), °C | 1010 | |
| 1080 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 390 |
| Thermal Conductivity, W/m-K | 120 | |
| 350 |
| Thermal Expansion, µm/m-K | 18 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 28 | |
| 92 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 29 | |
| 92 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 30 | |
| 31 |
| Density, g/cm3 | 8.7 | |
| 9.0 |
| Embodied Carbon, kg CO2/kg material | 2.8 | |
| 2.6 |
| Embodied Energy, MJ/kg | 45 | |
| 41 |
| Embodied Water, L/kg | 330 | |
| 310 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 11 to 120 | |
| 15 to 88 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 160 to 1340 | |
| 24 to 600 |
| Stiffness to Weight: Axial, points | 7.1 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 18 | |
| 18 |
| Strength to Weight: Axial, points | 11 to 18 | |
| 6.8 to 12 |
| Strength to Weight: Bending, points | 12 to 17 | |
| 9.1 to 13 |
| Thermal Diffusivity, mm2/s | 37 | |
| 100 |
| Thermal Shock Resistance, points | 12 to 20 | |
| 7.8 to 13 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Copper (Cu), % | 89 to 93 | |
| 99.95 to 99.995 |
| Iron (Fe), % | 0 to 0.050 | |
| 0 |
| Lead (Pb), % | 0 to 0.1 | |
| 0 |
| Phosphorus (P), % | 0 | |
| 0.0050 to 0.012 |
| Tin (Sn), % | 1.5 to 2.2 | |
| 0 |
| Zinc (Zn), % | 4.2 to 9.5 | |
| 0 |
| Residuals, % | 0 to 0.5 | |
| 0 |