C41500 Brass vs. C33200 Brass

Both C41500 brass and C33200 brass are copper alloys. They have 74% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is C41500 brass and the bottom bar is C33200 brass.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
100
Elongation at Break, % 2.0 to 42
7.0 to 60
Poisson's Ratio 0.33
0.31
Rockwell Superficial 30T Hardness 36 to 75
26 to 69
Shear Modulus, GPa 42
40
Shear Strength, MPa 220 to 360
240 to 300
Tensile Strength: Ultimate (UTS), MPa 340 to 560
320 to 520
Tensile Strength: Yield (Proof), MPa 190 to 550
110 to 450

Thermal Properties

Latent Heat of Fusion, J/g 200
170
Maximum Temperature: Mechanical, °C 180
130
Melting Completion (Liquidus), °C 1030
930
Melting Onset (Solidus), °C 1010
900
Specific Heat Capacity, J/kg-K 380
380
Thermal Conductivity, W/m-K 120
120
Thermal Expansion, µm/m-K 18
20

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 28
26
Electrical Conductivity: Equal Weight (Specific), % IACS 29
28

Otherwise Unclassified Properties

Base Metal Price, % relative 30
24
Density, g/cm3 8.7
8.2
Embodied Carbon, kg CO2/kg material 2.8
2.6
Embodied Energy, MJ/kg 45
44
Embodied Water, L/kg 330
320

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 11 to 120
35 to 150
Resilience: Unit (Modulus of Resilience), kJ/m3 160 to 1340
60 to 960
Stiffness to Weight: Axial, points 7.1
7.1
Stiffness to Weight: Bending, points 18
19
Strength to Weight: Axial, points 11 to 18
11 to 17
Strength to Weight: Bending, points 12 to 17
13 to 17
Thermal Diffusivity, mm2/s 37
37
Thermal Shock Resistance, points 12 to 20
11 to 17

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Copper (Cu), % 89 to 93
65 to 68
Iron (Fe), % 0 to 0.050
0 to 0.070
Lead (Pb), % 0 to 0.1
1.5 to 2.5
Tin (Sn), % 1.5 to 2.2
0
Zinc (Zn), % 4.2 to 9.5
29 to 33.5
Residuals, % 0 to 0.5
0 to 0.4

Comparable Variants