C41500 Brass vs. C37000 Muntz Metal
Both C41500 brass and C37000 Muntz Metal are copper alloys. They have 68% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is C41500 brass and the bottom bar is C37000 Muntz Metal.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 100 |
| Elongation at Break, % | 2.0 to 42 | |
| 40 |
| Poisson's Ratio | 0.33 | |
| 0.31 |
| Rockwell B Hardness | 62 to 90 | |
| 45 |
| Shear Modulus, GPa | 42 | |
| 39 |
| Shear Strength, MPa | 220 to 360 | |
| 270 |
| Tensile Strength: Ultimate (UTS), MPa | 340 to 560 | |
| 400 |
| Tensile Strength: Yield (Proof), MPa | 190 to 550 | |
| 160 |
Thermal Properties
| Latent Heat of Fusion, J/g | 200 | |
| 170 |
| Maximum Temperature: Mechanical, °C | 180 | |
| 120 |
| Melting Completion (Liquidus), °C | 1030 | |
| 900 |
| Melting Onset (Solidus), °C | 1010 | |
| 890 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 380 |
| Thermal Conductivity, W/m-K | 120 | |
| 120 |
| Thermal Expansion, µm/m-K | 18 | |
| 21 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 28 | |
| 27 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 29 | |
| 30 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 30 | |
| 23 |
| Density, g/cm3 | 8.7 | |
| 8.1 |
| Embodied Carbon, kg CO2/kg material | 2.8 | |
| 2.7 |
| Embodied Energy, MJ/kg | 45 | |
| 45 |
| Embodied Water, L/kg | 330 | |
| 320 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 11 to 120 | |
| 130 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 160 to 1340 | |
| 120 |
| Stiffness to Weight: Axial, points | 7.1 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 18 | |
| 19 |
| Strength to Weight: Axial, points | 11 to 18 | |
| 14 |
| Strength to Weight: Bending, points | 12 to 17 | |
| 15 |
| Thermal Diffusivity, mm2/s | 37 | |
| 39 |
| Thermal Shock Resistance, points | 12 to 20 | |
| 13 |
Alloy Composition
| Copper (Cu), % | 89 to 93 | |
| 59 to 62 |
| Iron (Fe), % | 0 to 0.050 | |
| 0 to 0.15 |
| Lead (Pb), % | 0 to 0.1 | |
| 0.8 to 1.5 |
| Tin (Sn), % | 1.5 to 2.2 | |
| 0 |
| Zinc (Zn), % | 4.2 to 9.5 | |
| 36 to 40.2 |
| Residuals, % | 0 | |
| 0 to 0.4 |