C41500 Brass vs. C78200 Nickel Silver
Both C41500 brass and C78200 nickel silver are copper alloys. They have 72% of their average alloy composition in common.
For each property being compared, the top bar is C41500 brass and the bottom bar is C78200 nickel silver.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 110 |
| Elongation at Break, % | 2.0 to 42 | |
| 3.0 to 40 |
| Poisson's Ratio | 0.33 | |
| 0.32 |
| Rockwell B Hardness | 62 to 90 | |
| 65 to 90 |
| Rockwell Superficial 30T Hardness | 36 to 75 | |
| 63 to 75 |
| Shear Modulus, GPa | 42 | |
| 43 |
| Shear Strength, MPa | 220 to 360 | |
| 280 to 400 |
| Tensile Strength: Ultimate (UTS), MPa | 340 to 560 | |
| 370 to 630 |
| Tensile Strength: Yield (Proof), MPa | 190 to 550 | |
| 170 to 570 |
Thermal Properties
| Latent Heat of Fusion, J/g | 200 | |
| 190 |
| Maximum Temperature: Mechanical, °C | 180 | |
| 160 |
| Melting Completion (Liquidus), °C | 1030 | |
| 1000 |
| Melting Onset (Solidus), °C | 1010 | |
| 970 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 390 |
| Thermal Conductivity, W/m-K | 120 | |
| 48 |
| Thermal Expansion, µm/m-K | 18 | |
| 19 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 28 | |
| 11 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 29 | |
| 12 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 30 | |
| 28 |
| Density, g/cm3 | 8.7 | |
| 8.4 |
| Embodied Carbon, kg CO2/kg material | 2.8 | |
| 3.3 |
| Embodied Energy, MJ/kg | 45 | |
| 52 |
| Embodied Water, L/kg | 330 | |
| 310 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 11 to 120 | |
| 18 to 120 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 160 to 1340 | |
| 130 to 1440 |
| Stiffness to Weight: Axial, points | 7.1 | |
| 7.4 |
| Stiffness to Weight: Bending, points | 18 | |
| 19 |
| Strength to Weight: Axial, points | 11 to 18 | |
| 12 to 21 |
| Strength to Weight: Bending, points | 12 to 17 | |
| 14 to 19 |
| Thermal Diffusivity, mm2/s | 37 | |
| 15 |
| Thermal Shock Resistance, points | 12 to 20 | |
| 12 to 21 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Copper (Cu), % | 89 to 93 | |
| 63 to 67 |
| Iron (Fe), % | 0 to 0.050 | |
| 0 to 0.35 |
| Lead (Pb), % | 0 to 0.1 | |
| 1.5 to 2.5 |
| Manganese (Mn), % | 0 | |
| 0 to 0.5 |
| Nickel (Ni), % | 0 | |
| 7.0 to 9.0 |
| Tin (Sn), % | 1.5 to 2.2 | |
| 0 |
| Zinc (Zn), % | 4.2 to 9.5 | |
| 20.2 to 28.5 |
| Residuals, % | 0 to 0.5 | |
| 0 to 0.5 |