C41500 Brass vs. R30001 Cobalt

C41500 brass belongs to the copper alloys classification, while R30001 cobalt belongs to the cobalt alloys. There are 23 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is C41500 brass and the bottom bar is R30001 cobalt.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
220
Elongation at Break, % 2.0 to 42
1.0
Poisson's Ratio 0.33
0.28
Shear Modulus, GPa 42
86
Tensile Strength: Ultimate (UTS), MPa 340 to 560
620

Thermal Properties

Latent Heat of Fusion, J/g 200
310
Melting Completion (Liquidus), °C 1030
1530
Melting Onset (Solidus), °C 1010
1260
Specific Heat Capacity, J/kg-K 380
430
Thermal Conductivity, W/m-K 120
15
Thermal Expansion, µm/m-K 18
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 28
1.8
Electrical Conductivity: Equal Weight (Specific), % IACS 29
1.8

Otherwise Unclassified Properties

Density, g/cm3 8.7
9.0
Embodied Carbon, kg CO2/kg material 2.8
8.9
Embodied Energy, MJ/kg 45
130
Embodied Water, L/kg 330
460

Common Calculations

Stiffness to Weight: Axial, points 7.1
14
Stiffness to Weight: Bending, points 18
22
Strength to Weight: Axial, points 11 to 18
19
Strength to Weight: Bending, points 12 to 17
18
Thermal Diffusivity, mm2/s 37
3.7
Thermal Shock Resistance, points 12 to 20
19

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0
2.0 to 3.0
Chromium (Cr), % 0
28 to 32
Cobalt (Co), % 0
43 to 59
Copper (Cu), % 89 to 93
0
Iron (Fe), % 0 to 0.050
0 to 3.0
Lead (Pb), % 0 to 0.1
0
Molybdenum (Mo), % 0
0 to 1.0
Nickel (Ni), % 0
0 to 3.0
Silicon (Si), % 0
0 to 2.0
Tin (Sn), % 1.5 to 2.2
0
Tungsten (W), % 0
11 to 13
Zinc (Zn), % 4.2 to 9.5
0
Residuals, % 0 to 0.5
0