C42600 Brass vs. C62300 Bronze
Both C42600 brass and C62300 bronze are copper alloys. They have 87% of their average alloy composition in common.
For each property being compared, the top bar is C42600 brass and the bottom bar is C62300 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 110 |
| Elongation at Break, % | 1.1 to 40 | |
| 18 to 32 |
| Poisson's Ratio | 0.33 | |
| 0.34 |
| Shear Modulus, GPa | 42 | |
| 43 |
| Shear Strength, MPa | 280 to 470 | |
| 360 to 390 |
| Tensile Strength: Ultimate (UTS), MPa | 410 to 830 | |
| 570 to 630 |
| Tensile Strength: Yield (Proof), MPa | 220 to 810 | |
| 230 to 310 |
Thermal Properties
| Latent Heat of Fusion, J/g | 200 | |
| 230 |
| Maximum Temperature: Mechanical, °C | 180 | |
| 220 |
| Melting Completion (Liquidus), °C | 1030 | |
| 1050 |
| Melting Onset (Solidus), °C | 1010 | |
| 1040 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 440 |
| Thermal Conductivity, W/m-K | 110 | |
| 54 |
| Thermal Expansion, µm/m-K | 18 | |
| 18 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 25 | |
| 12 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 26 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 31 | |
| 28 |
| Density, g/cm3 | 8.7 | |
| 8.3 |
| Embodied Carbon, kg CO2/kg material | 2.9 | |
| 3.1 |
| Embodied Energy, MJ/kg | 48 | |
| 52 |
| Embodied Water, L/kg | 340 | |
| 390 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 9.4 to 140 | |
| 95 to 150 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 230 to 2970 | |
| 240 to 430 |
| Stiffness to Weight: Axial, points | 7.1 | |
| 7.6 |
| Stiffness to Weight: Bending, points | 18 | |
| 19 |
| Strength to Weight: Axial, points | 13 to 27 | |
| 19 to 21 |
| Strength to Weight: Bending, points | 14 to 23 | |
| 18 to 20 |
| Thermal Diffusivity, mm2/s | 33 | |
| 15 |
| Thermal Shock Resistance, points | 15 to 29 | |
| 20 to 22 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 8.5 to 10 |
| Copper (Cu), % | 87 to 90 | |
| 83.2 to 89.5 |
| Iron (Fe), % | 0.050 to 0.2 | |
| 2.0 to 4.0 |
| Lead (Pb), % | 0 to 0.050 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 0 to 0.5 |
| Nickel (Ni), % | 0.050 to 0.2 | |
| 0 to 1.0 |
| Phosphorus (P), % | 0.020 to 0.050 | |
| 0 |
| Silicon (Si), % | 0 | |
| 0 to 0.25 |
| Tin (Sn), % | 2.5 to 4.0 | |
| 0 to 0.6 |
| Zinc (Zn), % | 5.3 to 10.4 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.5 |