C43500 Brass vs. Grade 8 Babbitt Metal
C43500 brass belongs to the copper alloys classification, while grade 8 Babbitt Metal belongs to the otherwise unclassified metals. There are 19 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is C43500 brass and the bottom bar is grade 8 Babbitt Metal.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 24 |
| Poisson's Ratio | 0.32 | |
| 0.41 |
| Shear Modulus, GPa | 42 | |
| 8.5 |
| Tensile Strength: Yield (Proof), MPa | 120 to 480 | |
| 23 |
Thermal Properties
| Latent Heat of Fusion, J/g | 190 | |
| 46 |
| Melting Completion (Liquidus), °C | 1000 | |
| 270 |
| Melting Onset (Solidus), °C | 970 | |
| 240 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 150 |
| Thermal Conductivity, W/m-K | 120 | |
| 24 |
| Thermal Expansion, µm/m-K | 19 | |
| 24 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 28 | |
| 19 |
| Density, g/cm3 | 8.5 | |
| 10 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 3.9 |
| Embodied Energy, MJ/kg | 45 | |
| 53 |
| Embodied Water, L/kg | 320 | |
| 840 |
Common Calculations
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 65 to 1040 | |
| 11 |
| Stiffness to Weight: Axial, points | 7.2 | |
| 1.3 |
| Stiffness to Weight: Bending, points | 19 | |
| 9.2 |
| Thermal Diffusivity, mm2/s | 37 | |
| 16 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 | |
| 0 to 0.0050 |
| Antimony (Sb), % | 0 | |
| 14 to 16 |
| Arsenic (As), % | 0 | |
| 0.3 to 0.6 |
| Bismuth (Bi), % | 0 | |
| 0 to 0.1 |
| Cadmium (Cd), % | 0 | |
| 0 to 0.050 |
| Copper (Cu), % | 79 to 83 | |
| 0 to 0.5 |
| Iron (Fe), % | 0 to 0.050 | |
| 0 to 0.1 |
| Lead (Pb), % | 0 to 0.090 | |
| 77.1 to 81.2 |
| Tin (Sn), % | 0.6 to 1.2 | |
| 4.5 to 5.5 |
| Zinc (Zn), % | 15.4 to 20.4 | |
| 0 to 0.0050 |
| Residuals, % | 0 to 0.3 | |
| 0 |