C43500 Brass vs. C38000 Brass
Both C43500 brass and C38000 brass are copper alloys. They have 76% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is C43500 brass and the bottom bar is C38000 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 100 |
| Elongation at Break, % | 8.5 to 46 | |
| 17 |
| Poisson's Ratio | 0.32 | |
| 0.31 |
| Shear Modulus, GPa | 42 | |
| 39 |
| Shear Strength, MPa | 220 to 310 | |
| 230 |
| Tensile Strength: Ultimate (UTS), MPa | 320 to 530 | |
| 380 |
| Tensile Strength: Yield (Proof), MPa | 120 to 480 | |
| 120 |
Thermal Properties
| Latent Heat of Fusion, J/g | 190 | |
| 170 |
| Maximum Temperature: Mechanical, °C | 160 | |
| 110 |
| Melting Completion (Liquidus), °C | 1000 | |
| 800 |
| Melting Onset (Solidus), °C | 970 | |
| 760 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 380 |
| Thermal Conductivity, W/m-K | 120 | |
| 110 |
| Thermal Expansion, µm/m-K | 19 | |
| 21 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 28 | |
| 22 |
| Density, g/cm3 | 8.5 | |
| 8.0 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 2.7 |
| Embodied Energy, MJ/kg | 45 | |
| 46 |
| Embodied Water, L/kg | 320 | |
| 330 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 44 to 120 | |
| 50 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 65 to 1040 | |
| 74 |
| Stiffness to Weight: Axial, points | 7.2 | |
| 7.1 |
| Stiffness to Weight: Bending, points | 19 | |
| 19 |
| Strength to Weight: Axial, points | 10 to 17 | |
| 13 |
| Strength to Weight: Bending, points | 12 to 17 | |
| 14 |
| Thermal Diffusivity, mm2/s | 37 | |
| 37 |
| Thermal Shock Resistance, points | 11 to 18 | |
| 13 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 | |
| 0 to 0.5 |
| Copper (Cu), % | 79 to 83 | |
| 55 to 60 |
| Iron (Fe), % | 0 to 0.050 | |
| 0 to 0.35 |
| Lead (Pb), % | 0 to 0.090 | |
| 1.5 to 2.5 |
| Tin (Sn), % | 0.6 to 1.2 | |
| 0 to 0.3 |
| Zinc (Zn), % | 15.4 to 20.4 | |
| 35.9 to 43.5 |
| Residuals, % | 0 to 0.3 | |
| 0 to 0.5 |