C44400 Brass vs. Grade N12MV Nickel

C44400 brass belongs to the copper alloys classification, while grade N12MV nickel belongs to the nickel alloys. There are 22 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is C44400 brass and the bottom bar is grade N12MV nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
220
Poisson's Ratio 0.32
0.31
Shear Modulus, GPa 41
84
Tensile Strength: Ultimate (UTS), MPa 350
600
Tensile Strength: Yield (Proof), MPa 120
310

Thermal Properties

Latent Heat of Fusion, J/g 180
320
Maximum Temperature: Mechanical, °C 140
900
Melting Completion (Liquidus), °C 940
1620
Melting Onset (Solidus), °C 900
1570
Specific Heat Capacity, J/kg-K 380
390
Thermal Expansion, µm/m-K 20
10

Otherwise Unclassified Properties

Base Metal Price, % relative 26
75
Density, g/cm3 8.3
9.2
Embodied Carbon, kg CO2/kg material 2.8
16
Embodied Energy, MJ/kg 46
200
Embodied Water, L/kg 330
260

Common Calculations

Resilience: Unit (Modulus of Resilience), kJ/m3 65
220
Stiffness to Weight: Axial, points 7.2
13
Stiffness to Weight: Bending, points 19
22
Strength to Weight: Axial, points 12
18
Strength to Weight: Bending, points 13
17
Thermal Shock Resistance, points 12
19

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Antimony (Sb), % 0.020 to 0.1
0
Carbon (C), % 0
0 to 0.12
Chromium (Cr), % 0
0 to 1.0
Copper (Cu), % 70 to 73
0
Iron (Fe), % 0 to 0.060
4.0 to 6.0
Lead (Pb), % 0 to 0.070
0
Manganese (Mn), % 0
0 to 1.0
Molybdenum (Mo), % 0
26 to 30
Nickel (Ni), % 0
60.2 to 69.8
Phosphorus (P), % 0
0 to 0.040
Silicon (Si), % 0
0 to 1.0
Sulfur (S), % 0
0 to 0.030
Tin (Sn), % 0.9 to 1.2
0
Vanadium (V), % 0
0.2 to 0.6
Zinc (Zn), % 25.2 to 29.1
0
Residuals, % 0 to 0.4
0