C44400 Brass vs. Grey Cast Iron
C44400 brass belongs to the copper alloys classification, while grey cast iron belongs to the iron alloys. There are 25 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is C44400 brass and the bottom bar is grey cast iron.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 180 |
| Poisson's Ratio | 0.32 | |
| 0.29 |
| Shear Modulus, GPa | 41 | |
| 69 |
| Tensile Strength: Ultimate (UTS), MPa | 350 | |
| 160 to 450 |
| Tensile Strength: Yield (Proof), MPa | 120 | |
| 98 to 290 |
Thermal Properties
| Latent Heat of Fusion, J/g | 180 | |
| 280 |
| Melting Completion (Liquidus), °C | 940 | |
| 1380 |
| Melting Onset (Solidus), °C | 900 | |
| 1180 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 490 |
| Thermal Conductivity, W/m-K | 110 | |
| 46 |
| Thermal Expansion, µm/m-K | 20 | |
| 11 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 25 | |
| 7.4 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 27 | |
| 8.9 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 26 | |
| 1.9 |
| Density, g/cm3 | 8.3 | |
| 7.5 |
| Embodied Carbon, kg CO2/kg material | 2.8 | |
| 1.5 |
| Embodied Energy, MJ/kg | 46 | |
| 21 |
| Embodied Water, L/kg | 330 | |
| 44 |
Common Calculations
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 65 | |
| 27 to 240 |
| Stiffness to Weight: Axial, points | 7.2 | |
| 13 |
| Stiffness to Weight: Bending, points | 19 | |
| 25 |
| Strength to Weight: Axial, points | 12 | |
| 5.8 to 17 |
| Strength to Weight: Bending, points | 13 | |
| 8.7 to 17 |
| Thermal Diffusivity, mm2/s | 35 | |
| 13 |
| Thermal Shock Resistance, points | 12 | |
| 6.0 to 17 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Antimony (Sb), % | 0.020 to 0.1 | |
| 0 |
| Carbon (C), % | 0 | |
| 3.1 to 3.4 |
| Copper (Cu), % | 70 to 73 | |
| 0 |
| Iron (Fe), % | 0 to 0.060 | |
| 92.1 to 93.9 |
| Lead (Pb), % | 0 to 0.070 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 0.5 to 0.7 |
| Phosphorus (P), % | 0 | |
| 0 to 0.9 |
| Silicon (Si), % | 0 | |
| 2.5 to 2.8 |
| Sulfur (S), % | 0 | |
| 0 to 0.15 |
| Tin (Sn), % | 0.9 to 1.2 | |
| 0 |
| Zinc (Zn), % | 25.2 to 29.1 | |
| 0 |
| Residuals, % | 0 to 0.4 | |
| 0 |