C44400 Brass vs. Zamak 3
C44400 brass belongs to the copper alloys classification, while Zamak 3 belongs to the zinc alloys. They have a modest 27% of their average alloy composition in common, which, by itself, doesn't mean much. There are 26 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is C44400 brass and the bottom bar is Zamak 3.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 86 |
| Poisson's Ratio | 0.32 | |
| 0.25 |
| Shear Modulus, GPa | 41 | |
| 33 |
| Tensile Strength: Ultimate (UTS), MPa | 350 | |
| 280 |
| Tensile Strength: Yield (Proof), MPa | 120 | |
| 210 |
Thermal Properties
| Latent Heat of Fusion, J/g | 180 | |
| 120 |
| Maximum Temperature: Mechanical, °C | 140 | |
| 95 |
| Melting Completion (Liquidus), °C | 940 | |
| 390 |
| Melting Onset (Solidus), °C | 900 | |
| 380 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 410 |
| Thermal Conductivity, W/m-K | 110 | |
| 110 |
| Thermal Expansion, µm/m-K | 20 | |
| 27 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 25 | |
| 27 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 27 | |
| 38 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 26 | |
| 11 |
| Density, g/cm3 | 8.3 | |
| 6.4 |
| Embodied Carbon, kg CO2/kg material | 2.8 | |
| 3.0 |
| Embodied Energy, MJ/kg | 46 | |
| 57 |
| Embodied Water, L/kg | 330 | |
| 380 |
Common Calculations
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 65 | |
| 260 |
| Stiffness to Weight: Axial, points | 7.2 | |
| 7.5 |
| Stiffness to Weight: Bending, points | 19 | |
| 23 |
| Strength to Weight: Axial, points | 12 | |
| 12 |
| Strength to Weight: Bending, points | 13 | |
| 15 |
| Thermal Diffusivity, mm2/s | 35 | |
| 43 |
| Thermal Shock Resistance, points | 12 | |
| 8.6 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 | |
| 3.5 to 4.3 |
| Antimony (Sb), % | 0.020 to 0.1 | |
| 0 |
| Cadmium (Cd), % | 0 | |
| 0 to 0.0050 |
| Copper (Cu), % | 70 to 73 | |
| 0 to 0.25 |
| Iron (Fe), % | 0 to 0.060 | |
| 0 to 0.1 |
| Lead (Pb), % | 0 to 0.070 | |
| 0 to 0.0050 |
| Magnesium (Mg), % | 0 | |
| 0.020 to 0.060 |
| Nickel (Ni), % | 0 | |
| 0 to 0.020 |
| Silicon (Si), % | 0 | |
| 0 to 0.030 |
| Tin (Sn), % | 0.9 to 1.2 | |
| 0 to 0.0030 |
| Zinc (Zn), % | 25.2 to 29.1 | |
| 95.3 to 96.5 |
| Residuals, % | 0 to 0.4 | |
| 0 |