C44500 Brass vs. ASTM B628 Ag-Cu

C44500 brass belongs to the copper alloys classification, while ASTM B628 Ag-Cu belongs to the otherwise unclassified metals. They have a modest 28% of their average alloy composition in common, which, by itself, doesn't mean much. There are 17 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is C44500 brass and the bottom bar is ASTM B628 Ag-Cu.

UNS C44500 (CW707R) Admiralty Brass ASTM B628 Silver-Copper Eutectic Electrical Contact Alloy

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		110
Elastic (Young's, Tensile) Modulus, GPa		83

Poisson's Ratio		0.32
Poisson's Ratio		0.36

Shear Modulus, GPa		41
Shear Modulus, GPa		31

Tensile Strength: Ultimate (UTS), MPa		350
Tensile Strength: Ultimate (UTS), MPa		350 to 760

Thermal Properties

Latent Heat of Fusion, J/g		180
Latent Heat of Fusion, J/g		140

Melting Completion (Liquidus), °C		940
Melting Completion (Liquidus), °C		780

Melting Onset (Solidus), °C		900
Melting Onset (Solidus), °C		780

Specific Heat Capacity, J/kg-K		380
Specific Heat Capacity, J/kg-K		280

Thermal Expansion, µm/m-K		20
Thermal Expansion, µm/m-K		19

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS		25
Electrical Conductivity: Equal Volume, % IACS		84

Electrical Conductivity: Equal Weight (Specific), % IACS		27
Electrical Conductivity: Equal Weight (Specific), % IACS		75

Otherwise Unclassified Properties

Density, g/cm³		8.3
Density, g/cm³		10

Common Calculations

Stiffness to Weight: Axial, points		7.2
Stiffness to Weight: Axial, points		4.6

Stiffness to Weight: Bending, points		19
Stiffness to Weight: Bending, points		14

Strength to Weight: Axial, points		12
Strength to Weight: Axial, points		9.5 to 21

Strength to Weight: Bending, points		13
Strength to Weight: Bending, points		11 to 18

Thermal Shock Resistance, points		12
Thermal Shock Resistance, points		16 to 34

Alloy Composition

Aluminum (Al), %		0
Aluminum (Al), %		0 to 0.0050

Cadmium (Cd), %		0
Cadmium (Cd), %		0 to 0.050

Copper (Cu), %		70 to 73
Copper (Cu), %		26.6 to 29

Iron (Fe), %		0 to 0.060
Iron (Fe), %		0 to 0.050

Lead (Pb), %		0 to 0.070
Lead (Pb), %		0 to 0.030

Nickel (Ni), %		0
Nickel (Ni), %		0 to 0.010

Phosphorus (P), %		0.020 to 0.1
Phosphorus (P), %		0 to 0.030

Silver (Ag), %		0
Silver (Ag), %		71 to 73

Tin (Sn), %		0.9 to 1.2
Tin (Sn), %		0

Zinc (Zn), %		25.2 to 29.1
Zinc (Zn), %		0 to 0.060

Residuals, %		0
Residuals, %		0 to 0.21