C46200 Brass vs. C17300 Copper
Both C46200 brass and C17300 copper are copper alloys. They have 64% of their average alloy composition in common. There are 26 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is C46200 brass and the bottom bar is C17300 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 120 |
| Elongation at Break, % | 17 to 34 | |
| 3.0 to 23 |
| Poisson's Ratio | 0.31 | |
| 0.33 |
| Shear Modulus, GPa | 40 | |
| 45 |
| Shear Strength, MPa | 240 to 290 | |
| 320 to 790 |
| Tensile Strength: Ultimate (UTS), MPa | 370 to 480 | |
| 500 to 1380 |
| Tensile Strength: Yield (Proof), MPa | 120 to 290 | |
| 160 to 1200 |
Thermal Properties
| Latent Heat of Fusion, J/g | 170 | |
| 230 |
| Maximum Temperature: Mechanical, °C | 120 | |
| 270 |
| Melting Completion (Liquidus), °C | 840 | |
| 980 |
| Melting Onset (Solidus), °C | 800 | |
| 870 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 380 |
| Thermal Conductivity, W/m-K | 110 | |
| 110 |
| Thermal Expansion, µm/m-K | 20 | |
| 17 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.1 | |
| 8.8 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 9.4 |
| Embodied Energy, MJ/kg | 46 | |
| 150 |
| Embodied Water, L/kg | 330 | |
| 310 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 69 to 100 | |
| 40 to 88 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 72 to 400 | |
| 110 to 5410 |
| Stiffness to Weight: Axial, points | 7.2 | |
| 7.6 |
| Stiffness to Weight: Bending, points | 19 | |
| 19 |
| Strength to Weight: Axial, points | 13 to 16 | |
| 16 to 44 |
| Strength to Weight: Bending, points | 14 to 17 | |
| 16 to 31 |
| Thermal Diffusivity, mm2/s | 35 | |
| 32 |
| Thermal Shock Resistance, points | 12 to 16 | |
| 17 to 48 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 | |
| 0 to 0.2 |
| Beryllium (Be), % | 0 | |
| 1.8 to 2.0 |
| Copper (Cu), % | 62 to 65 | |
| 95.5 to 97.8 |
| Iron (Fe), % | 0 to 0.1 | |
| 0 to 0.4 |
| Lead (Pb), % | 0 to 0.2 | |
| 0.2 to 0.6 |
| Nickel (Ni), % | 0 | |
| 0.2 to 0.6 |
| Silicon (Si), % | 0 | |
| 0 to 0.2 |
| Tin (Sn), % | 0.5 to 1.0 | |
| 0 |
| Zinc (Zn), % | 33.3 to 37.5 | |
| 0 |
| Residuals, % | 0 to 0.4 | |
| 0 to 0.5 |