C46200 Brass vs. C46400 Brass
Both C46200 brass and C46400 brass are copper alloys. They have a very high 97% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is C46200 brass and the bottom bar is C46400 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 100 |
| Elongation at Break, % | 17 to 34 | |
| 17 to 40 |
| Poisson's Ratio | 0.31 | |
| 0.31 |
| Shear Modulus, GPa | 40 | |
| 40 |
| Shear Strength, MPa | 240 to 290 | |
| 270 to 310 |
| Tensile Strength: Ultimate (UTS), MPa | 370 to 480 | |
| 400 to 500 |
| Tensile Strength: Yield (Proof), MPa | 120 to 290 | |
| 160 to 320 |
Thermal Properties
| Latent Heat of Fusion, J/g | 170 | |
| 170 |
| Maximum Temperature: Mechanical, °C | 120 | |
| 120 |
| Melting Completion (Liquidus), °C | 840 | |
| 900 |
| Melting Onset (Solidus), °C | 800 | |
| 890 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 380 |
| Thermal Conductivity, W/m-K | 110 | |
| 120 |
| Thermal Expansion, µm/m-K | 20 | |
| 21 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 24 | |
| 23 |
| Density, g/cm3 | 8.1 | |
| 8.0 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 2.7 |
| Embodied Energy, MJ/kg | 46 | |
| 47 |
| Embodied Water, L/kg | 330 | |
| 330 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 69 to 100 | |
| 76 to 140 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 72 to 400 | |
| 120 to 500 |
| Stiffness to Weight: Axial, points | 7.2 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 19 | |
| 20 |
| Strength to Weight: Axial, points | 13 to 16 | |
| 14 to 17 |
| Strength to Weight: Bending, points | 14 to 17 | |
| 15 to 17 |
| Thermal Diffusivity, mm2/s | 35 | |
| 38 |
| Thermal Shock Resistance, points | 12 to 16 | |
| 13 to 16 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Copper (Cu), % | 62 to 65 | |
| 59 to 62 |
| Iron (Fe), % | 0 to 0.1 | |
| 0 to 0.1 |
| Lead (Pb), % | 0 to 0.2 | |
| 0 to 0.2 |
| Tin (Sn), % | 0.5 to 1.0 | |
| 0.5 to 1.0 |
| Zinc (Zn), % | 33.3 to 37.5 | |
| 36.3 to 40.5 |
| Residuals, % | 0 to 0.4 | |
| 0 to 0.4 |