C46200 Brass vs. C61900 Bronze
Both C46200 brass and C61900 bronze are copper alloys. They have 64% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is C46200 brass and the bottom bar is C61900 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 110 |
| Elongation at Break, % | 17 to 34 | |
| 21 to 32 |
| Poisson's Ratio | 0.31 | |
| 0.34 |
| Shear Modulus, GPa | 40 | |
| 43 |
| Shear Strength, MPa | 240 to 290 | |
| 370 to 410 |
| Tensile Strength: Ultimate (UTS), MPa | 370 to 480 | |
| 570 to 650 |
| Tensile Strength: Yield (Proof), MPa | 120 to 290 | |
| 230 to 310 |
Thermal Properties
| Latent Heat of Fusion, J/g | 170 | |
| 230 |
| Maximum Temperature: Mechanical, °C | 120 | |
| 220 |
| Melting Completion (Liquidus), °C | 840 | |
| 1050 |
| Melting Onset (Solidus), °C | 800 | |
| 1040 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 440 |
| Thermal Conductivity, W/m-K | 110 | |
| 79 |
| Thermal Expansion, µm/m-K | 20 | |
| 18 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 24 | |
| 28 |
| Density, g/cm3 | 8.1 | |
| 8.3 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 3.1 |
| Embodied Energy, MJ/kg | 46 | |
| 51 |
| Embodied Water, L/kg | 330 | |
| 380 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 69 to 100 | |
| 110 to 150 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 72 to 400 | |
| 230 to 430 |
| Stiffness to Weight: Axial, points | 7.2 | |
| 7.6 |
| Stiffness to Weight: Bending, points | 19 | |
| 19 |
| Strength to Weight: Axial, points | 13 to 16 | |
| 19 to 22 |
| Strength to Weight: Bending, points | 14 to 17 | |
| 18 to 20 |
| Thermal Diffusivity, mm2/s | 35 | |
| 22 |
| Thermal Shock Resistance, points | 12 to 16 | |
| 20 to 23 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 | |
| 8.5 to 10 |
| Copper (Cu), % | 62 to 65 | |
| 83.6 to 88.5 |
| Iron (Fe), % | 0 to 0.1 | |
| 3.0 to 4.5 |
| Lead (Pb), % | 0 to 0.2 | |
| 0 to 0.020 |
| Tin (Sn), % | 0.5 to 1.0 | |
| 0 to 0.6 |
| Zinc (Zn), % | 33.3 to 37.5 | |
| 0 to 0.8 |
| Residuals, % | 0 to 0.4 | |
| 0 to 0.5 |